Abstract:A modified ZSM-5 zeolite (denoted as ZSM-5-M), which was synthesized using tetrapropylammonium hydroxide (TPAOH) and cetyltrimethylammonium bromide (CTAB) as dual templates, and the commercial ZSM-5 zeolite (denoted as ZSM-5-C), have been used to prepare the corresponding CuZSM-5 (M & C) catalysts containing 3 wt% Cu by ion exchange method. Compared to CuZSM-5-C catalyst, the CuZSM-5-M catalyst demonstrated remarkably higher catalytic activity at low temperatures (<450 °C) for selective catalytic reduction of NOx with NH3 both in the simulated exhaust and engine bench testing. The modified synthesis by the dual template with the product aged for a long time at room temperature, leads to the formation of the ZSM-5-M zeolite with much higher specific surface area (608 m2 g−1) and higher total pore volume (0.8880 cm3 g−1) due to the presence of more mesoporous pores. The X-ray diffraction results showed that ZSM-5-M maintained its typical MFI structure, while its crystallinity (84.1%) was lower than that of the ZSM-5-C zeolite. The characterization results by H2 temperature-programmed reduction and X-ray photoelectron spectra revealed that the higher redox properties of isolated Cu2+ ions combined with the high-dispersion CuO crystallites and Cu+ ions are likely the main cause for the excellent low-temperature activity of the CuZSM-5-M catalysts. The isolated active Cu2+ species and high-dispersion CuO crystallites had a stronger interaction with other atoms in CuZSM-5-M catalysts. The results from thermogravimetric analysis, temperature-programmed desorption of ammonia and in situ diffuse reflectance infrared Fourier transform spectroscopy demonstrated that ZSM-5-M is a strong Bronsted acid site and the CuZSM-5-M catalyst had a relatively higher exchange rate of Cu2+ and Cu+ ions and more Lewis acidic sites, giving it a high NH3 adsorption capacity. The strong Bronsted acid site might be another cause that results in the higher NH3-SCR performance of the CuZSM-5-M catalyst.

Self-synthesis and performance analysis of a Cu-Fe composite ZSM-5 zeolitic catalyst for NOx reduction and particulate matter removal using NH3 SCR

Highly Efficient Fe-Cu/CL Catalysts Based on Low-Cost Clay Minerals for NH3-SCR of NOx at Low Temperature

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

One-pot synthesis of Fe/Cu-SSZ-13 catalyst and its highly efficient performance for the selective catalytic reduction of nitrogen oxide with ammonia

Hybrid Cu-Fe/ZSM-5 Catalyst Prepared by Liquid Ion-Exchange for NOx Removal by NH3-SCR Process

Influence of Fe–Cu-SSZ-13 and hybrid Fe–Cu-SSZ-13 zeolite catalyst in ammonia-selective catalytic reduction (NH3-SCR) of NOx

Synthesis and evaluation of mesopore structured ZSM-5 and a CuZSM-5 catalyst for NH3-SCR reaction: Studies of simulated exhaust and engine bench testing

Design, Synthesis, and Insights into the Redox Mechanism of Highly Efficient One-Pot Cu-ZSM-5 Catalysts for the Reduction of NO x by NH 3 -SCR at Low Temperatures

Strong metal oxide-zeolite interactions during selective catalytic reduction of nitrogen oxides

Optimization of isolated copper species on the NH 3 -SCR performance over Cu/SSZ-39 modified by ammonia water

Iron-Based Composite Oxide Catalysts Tuned by CTAB Exhibit Superior NH3–SCR Performance

Hydrothermally stable metal oxide-zeolite composite catalysts for low-temperature NOx reduction with improved N2 selectivity

Characterization of Commercial Cu-SSZ-13 and Cu-SAPO-34 Catalysts with Hydrothermal Treatment for NH3-SCR of NOx in Diesel Exhaust

Effects of Catalyst Physicochemical Properties on the Catalytic Activity of Cu Zeolite Selective Catalytic Reduction at Different Inlet Gas Conditions

Design and Synthesis of Core-Shell Structured Meso-Cu-ssz-13@mesoporous Aluminosilicate Catalyst for SCR of NOx with NH3: Enhancement of Activity, Hydrothermal Stability and Propene Poisoning Resistance

Cu/Fe-UZM-35 Catalysts for NOx Abatement in Diesel Vehicles for Next-Stage Emission Standards

Enhanced hydrothermal stability of Cu-SSZ-13 by compositing with Cu-SAPO-34 in selective catalytic reduction of nitrogen oxides with ammonia

Experimental and Density Functional Theory Studies on the Zeolite-Based Fe–Ni–W Trimetallic Catalyst for High-Temperature NOx Selective Catalytic Reduction: Identification of Active Sites Suppressing Ammonia Over-oxidation

Effect of Fe Addition on the Structure and SCR Reactivity of One-Pot Synthesized Cu-SSZ-13

Micro-structured Cu-ZSM-5 catalyst on aluminum microfibers for selective catalytic reduction of NO by ammonia

A Study on Chemisorbed Oxygen and Reaction Process of Fe–CuOx/ZSM-5 Via Ultrasonic Impregnation Method for Low-Temperature NH3-SCR