Abstract:In this work, Ce and Mn were added to Cu-SSZ-39 zeolites by ion-exchange process, and their activity performance for selective catalytic reduction of NOx with ammonia (NH3-SCR), especially hydrothermal stability (hydrothermal aging at 750, 800, 850 °C) was investigated systematically. It is found that the addition of Ce and Mn, Mn more evidently, both can greatly improve the activity of Cu-SSZ-39 catalyst. Moreover, MnCu-SSZ-39 catalyst have shown superior hydrothermal stability compared with Cu-SSZ-39 catalyst, and outstandingly its activity is not only not decreased significantly like Cu-SSZ-39 but improved obviously after hydrothermal aging at as high as 850°C. The high and improved activity of Ce and Mn added Cu-SSZ-39 is ascribed to more active CuO crystallites formation in the inner channel and higher acidity strength. The superior hydrothermal stability of MnCu-SSZ-39 may be due to its well-preserved structure and acid density even after hydrothermal aging at as high as 850 °C. Moreover, during the hydrothermal aging process, not only Cu oxides aggregation is inhibited, but also more Cu2+ ion species are induced to ion exchange sites in MnCu-SSZ-39, which may account for its excellent hydrothermal stability (even higher than the activity of fresh samples). The mechanism analysis has shown NH3-SCR reaction over Cu-SSZ-39 and CeCu-SSZ-39 samples follow the "Langmuir−Hinshelwood" (L-H) mechanism, while on MnCu-SSZ-39, it follows both "L−H" and "Eley−Rideal" (E−R) mechanisms, which may also be another reason for its excellent activity and hydrothermal stability. Moreover, "Fast SCR" mechanisms also occur and contribute over hydrothermal aged A-MnCu-SSZ-39 sample, in addition to "L-H" and "E-R" mechanisms. Thus, the easily prepared MnCu-SSZ-39 catalyst has shown the excellent activity and super hydrothermal stability, with 90% NO conversion at 245 °C and broader temperature window of 245 °C to 550 °C, even after hydrothermal aging at 850 °C, therefore indicate great potential for future application in NOx purifying from diesel engine exhaust.

Strong metal oxide-zeolite interactions during selective catalytic reduction of nitrogen oxides

Investigation on the redox/acidic features of bimetallic MOF-derived CeMOx catalysts for low-temperature NH3-SCR of NOx

Promoting Metal Oxides–zeolite Electron Interaction on MnCeOx/HY Catalyst for Boosting Nitrogen Oxides Reduction

Mechanistic Insights into the Enhanced Low-Temperature Activity of Cu-SSZ-13 by MnOx-CeO2 Modification for Standard SCR Reaction and Fast SCR Reactions

Selective catalytic reduction of NOx with NH3 over Mn–Zr–Ti mixed oxide catalysts

MnOx-CeO2 Supported on Cu-SSZ-13: A Novel SCR Catalyst in a Wide Temperature Range

Design, Synthesis, and Insights into the Redox Mechanism of Highly Efficient One-Pot Cu-ZSM-5 Catalysts for the Reduction of NO x by NH 3 -SCR at Low Temperatures

Manganese Oxide Catalysts Supported on Zinc Oxide Nanorod Arrays: A New Composite for Selective Catalytic Reduction of NOx with NH3 at Low Temperature

Interface Induced by Hydrothermal Aging Boosts the Low-Temperature Activity of Cu-SSZ-13 for Selective Catalytic Reduction of NOx

Hydrothermally stable metal oxide-zeolite composite catalysts for low-temperature NOx reduction with improved N2 selectivity

MnOx location on MnOx-ZSM-5 to influence the catalytic activity for selective catalytic reduction of NOx by NH3

Effects of Catalyst Physicochemical Properties on the Catalytic Activity of Cu Zeolite Selective Catalytic Reduction at Different Inlet Gas Conditions

Basic understanding of Cu‐SSZ‐13 in catalyzing low‐temperature selective catalytic reduction of NOx by ammonia

Promoting effect of Ce and Mn addition on Cu-SSZ-39 zeolites for NH3-SCR reaction: Activity, hydrothermal stability, and mechanism study

Low-temperature Selective Catalytic Reduction of NOx with NH3 over Metal Oxide and Zeolite Catalysts—a Review

One-pot synthesis of Fe/Cu-SSZ-13 catalyst and its highly efficient performance for the selective catalytic reduction of nitrogen oxide with ammonia

Ce enhanced low-temperature performance of Mn modified Cu-Beta zeolite catalyst for NH 3 -SCR

Novel shielding and synergy effects of Mn-Ce oxides confined in mesoporous zeolite for low temperature selective catalytic reduction of NOx with enhanced SO2/H2O tolerance

Cu-OFF/ERI Zeolite: Intergrowth Structure Synergistically Boosting Selective Catalytic Reduction of NOx with NH3

Optimization of isolated copper species on the NH 3 -SCR performance over Cu/SSZ-39 modified by ammonia water

Design of robust Co-doped Mn3O4 spinel catalysts for selective catalytic reduction of NO with NH3 at low temperatures