Promoting effect of Ce and Mn addition on Cu-SSZ-39 zeolites for NH3-SCR reaction: Activity, hydrothermal stability, and mechanism study
Wang Yao,Li Gang-gang,Zhang Shao-qing,Zhang Xin-yan,Zhang Xin,Hao Zheng-ping
DOI: https://doi.org/10.1016/j.cej.2020.124782
IF: 15.1
2020-08-01
Chemical Engineering Journal
Abstract:<p>In this work, Ce and Mn were added to Cu-SSZ-39 zeolites by ion-exchange process, and their activity performance for selective catalytic reduction of NO<sub>x</sub> with ammonia (NH<sub>3</sub>-SCR), especially hydrothermal stability (hydrothermal aging at 750, 800, 850 °C) was investigated systematically. It is found that the addition of Ce and Mn, Mn more evidently, both can greatly improve the activity of Cu-SSZ-39 catalyst. Moreover, MnCu-SSZ-39 catalyst have shown superior hydrothermal stability compared with Cu-SSZ-39 catalyst, and outstandingly its activity is not only not decreased significantly like Cu-SSZ-39 but improved obviously after hydrothermal aging at as high as 850°C. The high and improved activity of Ce and Mn added Cu-SSZ-39 is ascribed to more active CuO crystallites formation in the inner channel and higher acidity strength. The superior hydrothermal stability of MnCu-SSZ-39 may be due to its well-preserved structure and acid density even after hydrothermal aging at as high as 850 °C. Moreover, during the hydrothermal aging process, not only Cu oxides aggregation is inhibited, but also more Cu<sup>2+</sup> ion species are induced to ion exchange sites in MnCu-SSZ-39, which may account for its excellent hydrothermal stability (even higher than the activity of fresh samples). The mechanism analysis has shown NH<sub>3</sub>-SCR reaction over Cu-SSZ-39 and CeCu-SSZ-39 samples follow the "Langmuir−Hinshelwood" (L-H) mechanism, while on MnCu-SSZ-39, it follows both "L−H" and "Eley−Rideal" (E−R) mechanisms, which may also be another reason for its excellent activity and hydrothermal stability. Moreover, "Fast SCR" mechanisms also occur and contribute over hydrothermal aged A-MnCu-SSZ-39 sample, in addition to "L-H" and "E-R" mechanisms. Thus, the easily prepared MnCu-SSZ-39 catalyst has shown the excellent activity and super hydrothermal stability, with 90% NO conversion at 245 °C and broader temperature window of 245 °C to 550 °C, even after hydrothermal aging at 850 °C, therefore indicate great potential for future application in NO<sub>x</sub> purifying from diesel engine exhaust.</p>
engineering, chemical, environmental