Abstract:WC-Co cemented carbides are widely used in the fields of military, aerospace, mining and cutting industry etc. In this paper, a new two-step method for the preparation of WC-Co cemented carbides was proposed. First, the mixture of yellow tungsten trioxide (WO3) and cobaltic oxide (Co2O3) were reduced by carbon black to remove all the oxygen. Then, the carbothermic reduction products were precisely mixed with an appropriate amount of carbon black to directly prepare WC-Co cemented carbides. The effects of C/WO3 ratio on the phase composition, morphological evolution, particle size and mechanical properties of products are investigated. The experimental results revealed that when the C/WO3 molar ratio was above 2.7, all oxygen in the raw material mixture were removed by carbon black and a mixture of W2C and η-phase were obtained after the first step of carbothermic reduction at 1150 °C for 2 h; then, the mixture of carbothermic reduction product and an appropriate content of carbon black was compacted, and the green compact was first carbonized at 1200 °C for 2 h and then sintered at 1450 °C for 4 h to prepare cemented carbides. With the increase of C/WO3 ratio at the first stage, the content of η-phase with a low melting point increased, which resulted in the large grain size of WC in the finally prepared cemented carbide. Compared with the traditional method of preparing cemented carbides, the cemented carbides prepared by the current method showed a higher hardness and toughness. Furthermore, the addition of a proper content of the VC in the second stage can significantly inhibit the grain growth of WC and further increase the hardness of cemented carbides.

Preparation of Monophasic Tungsten boride powder from Tungsten and boron carbide

Preparation of ultrafine (W,Mo)B, (W,Mo)B2.5 and (Mo,W)AlB solid solution composite powders

Size-controlled preparations of tungsten and molybdenum borides in calcium or aluminum melt

Preparation of Submicron Boron Carbide Powder Through Gas-Solid Reaction Method

Synthesis of high entropy monoboride (Mo0.25W0.25Cr0.25Ta0.25)B powders with abundant twins from oxides

Synthesis, Phase Evolutions, and Stabilities of Boron-Rich Tungsten Borides at High Pressure.

Preparation of Nano-Zrb2 Powder by Ca Liquid Assisted Boronation Reaction Between ZrC and B4C

Synthesis of Ultra-Fine and High-Pure Zirconium Diboride Powders Using Solution-Based Processing

Boriding of tungsten by the powder-pack process: Phase formation, growth kinetics and enhanced neutron shielding

Fabrication and characterization of hot-pressed B-rich boron carbide

A Facile Route for the Synthesis of High‐entropy Transition Carbides/borides at Low Temperatures

Synthesis and Thermal Oxidation Resistance of Boron-Rich Boron-Carbide Material

High-pressure Synthesis of Tungsten Carbide–cubic Boron Nitride (wc–cbn) Composites: Effect of Cbn Particle Size and Volume Fraction on Their Microstructure and Properties

Low-temperature synthesis of high-purity boron carbide via an aromatic polymer precursor

Crystal structures and formation mechanisms of boron-rich tungsten borides

Preparation Technology of Ultra-Fine Tungsten Carbide Powders: an Overview

The Hydrothermal Method of Preparing Boron–Saccharide Precursors for the Synthesis of Boron Carbide and Its Influence on the Morphology and Phase Composition of the Obtained Products

A short and facile process to synthesize WC-Co cemented carbides

Ultrafine and Nanoscaled Tungsten Carbide Synthesis from Colloidal Carbon Coated Nano Tungsten Precursor

Research on the Evolution of Preparation of the Boron Carbide Power