Abstract:Two types of polysiloxanes, GVPMS and GVHMS, were synthesized through nonhydrolytic sol-gel reaction from vinyltrimethoxysilane(VTMS), 3-glycidoxypropyltrimethoxysilane(KH560) and diphenylsilandiol(DPSD) or hydroxyl silicone oil, respectively. The chemical structures were characterized by Fourier transform infrared (FTIR) spectroscopy, 1H nuclear magnetic resonance (1H-NMR) spectroscopy and gel permeation chromatography (GPC). GVPMS and GVHMS were used as adhesion promoter for addition-cure silicone rubber. It was found that the adhesion promoters not only greatly improved adhesion strength but also had excellent compatibility with silicone rubber. Among them, GVPMS gave better adhesion strength in silicone rubber. The shear strength of silicone rubber reached 1.70 MPa with addition of 1.5 phr GVPMS, which was about 317% higher than that of silicone rubber without the adhesion promoter. Meanwhile, the shear strength of silicone rubber reached 1.14 MPa with addition of 2.0 phr GVHMS, which was 183% higher than that of silicone rubber without the adhesion promoter. Optical property test results revealed that the refractive indexes of GVPMS and GVHMS were 1.5185 and 1.4133 respectively and both of them had good compatibility with silicone rubber, which satisfied the application demand of high-refractive and low-refractive electron encapsulation. Thermal resistance test and SEM results further proved that adhesion promoter could significantly increase the adhesion between the copper substrate and silicone rubber, in which GVPMS had a better performance. Oxidation treatment experiment further explained the mechanism that adhesion promoter functioned as a bridge, linked silicone rubber and copper substrate through chemical bonds.

Transparent organic silicon gel adhesive

High-transparency high-deep-layer-curing-speed double-component condensed organic silicon potting adhesive

Organize modification of silica sol and its application in adhesives

Preparation and Research on Silicone Liquid Optical Clear Adhesives

Research on Silicon-Glass Thermal Bonding with SiO2 Film Assist

Repositionable Pressure-Sensitive Adhesive Possessing Thermal-Stimuli Switchable Transparency

The Preparation of a Novel Silicone Optical Adhesive with Low Hardness and High Refractive Index

Preparation method of hydrosilylation/free radical dual-crosslinking organic silicon pressure-sensitive adhesive

The synthesis, characterization and properties of silicone adhesion promoters for addition-cure silicone rubber

Solvent-Resistant Adhesive Gel with Thermal Post-Tunability

Grafting Silicone at Room Temperature-a Transparent, Scratch-resistant Nonstick Molecular Coating

A new organosilicon adhesive based on polysiloxane and polysilazane

Ultraviolet (UV)-moisture double-curing liquid optical transparent adhesive and preparation method thereof

Synthesis of a siloxane oligomer containing ether bond for promoting the adhesion between addition-cure silicone rubber and polycarbonate (PC)

PREPARATION AND PROPERTIES OF TRANSPARENT COATING FOR POLYACRYLATES COPOLYMER MODIFIED WITH ORGANOSILICON

UV-Cured Transparent Silicone Materials with High Tensile Strength Prepared from Hyperbranched Silicon-Containing Polymers and Polyurethane-Acrylates

Development of Organosilicon Adhesive with Low Decomposition and High Temperature Resistance

A silica/PVA adhesive hybrid material with high transparency, thermostability and mechanical strength

Optimizing the fabrication of abrasion-resistant and transparent organosilicon coating

Synthesis and properties of optically clear silicone resin/epoxy resin hybrids

Synthesis and application of adhesion promoter containing phenolic hydroxyl/acrylate groups for addition-cure liquid silicone rubber