Smart Responsive Azo-Copolymer with Photoliquefaction for Switchable Adhesive Application
Ruiyang Zhao,Jiahui Mu,Jiayu Bai,Wenpeng Zhao,Piwen Gong,Longxuan Chen,Na Zhang,Xili Shang,Fusheng Liu,Shouke Yan
DOI: https://doi.org/10.1021/acsami.2c01556
2022-04-01
Abstract:The development and utilization of switchable adhesives are considered to be an essential target to solve the problems of their separation and recycling in some specific service environments, such as the preparation or repair process of electronic devices. Intelligent materials with controllable phase transition are utilized to fabricate switchable adhesives because of the significantly diverse adhesion strengths in different phase states. Photoresponsive azobenzene and its derivatives usually possess different melting temperatures (Tm) or/and glass transition temperatures (Tg) of the cis–trans isomers, which are beneficial to making the photoinduced solid–liquid phase transition for switchable adhesive application possible. Here, a novel three-component azo-copolymer (PNIM-Azo) with fast and reversible photoinduced solid–liquid phase transition has been designed and synthesized. PNIM-Azo possesses reversible bonding/debonding processes, resulting from the different adhesion strengths between trans-configuration PNIM-Azo in the solid state and cis-configuration in the liquid state. Moreover, by incorporating commercialized 2-methoxyethyl acrylate and N-isopropylacrylamide with O and N heteroatoms into the copolymer, the trans-configuration PNIM-Azo possesses the highest adhesion strength (∼11 MPa between two glass substrates) among all of the reported azobenzene-based switchable adhesives, which could be attributed to the increase in the entanglement effect because of the H-bond in the polymer chains formed by introducing heteroatoms. Our synthesized PNIM-Azo copolymer provides an alternative for designing and developing switchable adhesives with high adhesion strength for some electronic production processes.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.2c01556.Synthesis route of the sample (Figure S1); 1H NMR of M1 (Figure S2); 13C NMR of M1 (Figure S3); MS of M1 (Figure S4); 1H NMR of M2 (Figure S5); 13C NMR of M2 (Figure S6); MS of M2 (Figure S7); 1H NMR of PNIM-Azo (Figure S8); GPC curves of four PNIM-Azos (Figure S9); digital photograph of the PNIM-Azo-glued glasses substrates for shear test and schematic diagrams of the dimensions of PNIM-Azo-glued specimen (Figure S10); multiple cycles of trans–cis isomerization of PNIM-Azo-3 (Figure S11); time-resolution UV–vis spectra of PNIM-Azos (Figure S12); 1H NMR of PNIM-Azo-3 in liquid state and recovered back to original state (Figure S13); DSC curves of other three PNIM-Azos (Figure S14); digital photographs of photoinduced solid–liquid transition of PNIM-Azos (Figure S15); stress–strain curves of PNIM-Azo-3 glued on glass substrates by thermal-induced liquefaction (Figure S16); stress–strain curves of selected four commercial adhesives and PNIM-Azo-3 as adhesive glued on glass substrates (Figure S17); stress–strain curves of PNIM-Azo-3 glued on glasses substrates in trans- and cis-configuration (Figure S18); multiple-cycled adhesive strength difference of trans–cis isomerization of PNIM-Azo-3 (Figure S19); thermal infrared imaging photos of PE ring and PE ring bonded with PNIM-Azo-3 (Figure S20); digital photo of PNIM-Azo-1, PNIM-Azo-3, PNIM-Azo-6, and PNIM-Azo-15 in water and ultrasonic vibration for 30 min (Figure S21); correlation data of the typical commercial adhesion strength (Table S1) (PDF)Movie S1, showing a PE strip (dimensions of 10 cm × 6 mm × 0.3 mm) glued by PNIM-Azo-3 (5 mg) at one side to acquire a closed ring, which opened after irradiation on the adhesive position by 355 nm UV light for 1 min (MP4)Movie S2, showing bonded glasses can lift a weight of 200 g firmly for 5 h under water (shown at 25× speed) (MP4)Movie S3, showing that the adhesion strength of PNIM-Azo-3 was significantly reduced by 355 nm UV light irradiation on the adhesive position and that the weight fell off after irradiation for 5 min (MP4)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology