Abstract:Two types of polysiloxanes, GVPMS and GVHMS, were synthesized through nonhydrolytic sol-gel reaction from vinyltrimethoxysilane(VTMS), 3-glycidoxypropyltrimethoxysilane(KH560) and diphenylsilandiol(DPSD) or hydroxyl silicone oil, respectively. The chemical structures were characterized by Fourier transform infrared (FTIR) spectroscopy, 1H nuclear magnetic resonance (1H-NMR) spectroscopy and gel permeation chromatography (GPC). GVPMS and GVHMS were used as adhesion promoter for addition-cure silicone rubber. It was found that the adhesion promoters not only greatly improved adhesion strength but also had excellent compatibility with silicone rubber. Among them, GVPMS gave better adhesion strength in silicone rubber. The shear strength of silicone rubber reached 1.70 MPa with addition of 1.5 phr GVPMS, which was about 317% higher than that of silicone rubber without the adhesion promoter. Meanwhile, the shear strength of silicone rubber reached 1.14 MPa with addition of 2.0 phr GVHMS, which was 183% higher than that of silicone rubber without the adhesion promoter. Optical property test results revealed that the refractive indexes of GVPMS and GVHMS were 1.5185 and 1.4133 respectively and both of them had good compatibility with silicone rubber, which satisfied the application demand of high-refractive and low-refractive electron encapsulation. Thermal resistance test and SEM results further proved that adhesion promoter could significantly increase the adhesion between the copper substrate and silicone rubber, in which GVPMS had a better performance. Oxidation treatment experiment further explained the mechanism that adhesion promoter functioned as a bridge, linked silicone rubber and copper substrate through chemical bonds.

A new organosilicon adhesive based on polysiloxane and polysilazane

Structure and properties of novel silicone polyamine as epoxy resin curing agents

Organize modification of silica sol and its application in adhesives

The Effect of Silane Coupling Agent Containing Methacryloxy Group on UV-Curable Acrylate-Modified Polyurethane/SiO2 Hybrid Coatings

Development of Organosilicon Adhesive with Low Decomposition and High Temperature Resistance

The Preparation of a Novel Silicone Optical Adhesive with Low Hardness and High Refractive Index

Preparation Of Nanosilica Reinforced Waterborne Silylated Polyether Adhesive With High Shear Strength

Synthesis and application of adhesion promoter containing phenolic hydroxyl/acrylate groups for addition-cure liquid silicone rubber

Synthesis of UV rapid curing silicone coatings via photoinitiated thiol-ene click polymerization for pressure-sensitive adhesive

Synthesis of an adhesion-enhancing polyhydrosiloxane containing acrylate groups and its cross-linked addition-cure silicone encapsulant

Preparation and Thermal Stability of Phosphorus Acrylic Latex Modified with Organic Silicon

UV-curable silicone pressure-sensitive adhesive based on thiol-ene reaction

The synthesis, characterization and properties of silicone adhesion promoters for addition-cure silicone rubber

Mechanical properties and thermal stability of ambient-cured thick polysiloxane coatings prepared by a sol-gel process of organoalkoxysilanes

The synthesis and research of a novel organosilicon-modified waterborne blocked polyisocyanate crosslinker with a semi-interpenetrating network structure

Thermally Stable UV-Curable Pressure-Sensitive Adhesives Based on Silicon-Acrylate Telomers and Selected Adhesion Promoters

Development and Study of a New Silane Based Polyurethane Hybrid Flexible Adhesive-Part 1: Mechanical Characterization

Synthesis of a siloxane oligomer containing ether bond for promoting the adhesion between addition-cure silicone rubber and polycarbonate (PC)

Silanization as a strategy to design polyurethane-acrylic hybrid pressure-sensitive adhesives

Promoters for Improved Adhesion Strength between Addition-Cured Liquid Silicone Rubber and Low-Melting-Point Thermoplastic Polyurethanes

Amino acid-modified polysiloxane for superior metal bonding and antimicrobial coatings