UV-curable silicone pressure-sensitive adhesive based on thiol-ene reaction

Yu Zhou,Zuyi Zhao,Zhaoxia Liu,Hongxiang Chen,Hongye Yan,Junjie Tan,Fan Li
DOI: https://doi.org/10.1016/j.porgcoat.2023.107954
IF: 6.6
2023-09-20
Progress in Organic Coatings
Abstract:In order to improve the curing efficiency and reduce energy consumption of silicone pressure-sensitive adhesive (SiPSA), a kind of UV-curable SiPSA based on thiol-ene reaction was prepared with methyl vinyl MQ resin as hard segment, methyl vinyl silicone rubber (110-2S) as soft segment and mercaptyl silicone oil as cross-linker. The UV-cured SiPSA exhibited excellent thermal stability and water resistance. Its physical features such as chemical composition, cross-linking extent and dispersion of MQ resin in silicone rubber were directly related to the vinyl content in MQ resin, the thiol/ene ratio and the resin/rubber ratio, which further affected mechanical properties and adhesive properties of SiPSA. With the vinyl content in MQ resin of 56 mmol/100 g, the thiol/ene molar ratio of 0.8 and the resin/rubber mass ratio of 1.4, the UV-cured SiPSA-B1.4–0.8 had better mechanical properties, moreover it had higher tensile shear strength of >2.0 MPa and showed interface failure on the surface of substrates, indicating that it had great potential applications as PSA.
materials science, coatings & films,chemistry, applied
What problem does this paper attempt to address?
The problem this paper attempts to address is to improve the curing efficiency of silicone pressure-sensitive adhesives (SiPSA) and reduce energy consumption. Specifically, the authors prepared a novel UV-cured silicone pressure-sensitive adhesive (UV-cured SiPSA) using UV curing technology based on thiol-ene reaction. This new material can be rapidly cured at room temperature through UV irradiation and has many advantages, such as simple process, high curing efficiency, and energy saving. The main research contents of the paper include: 1. **Material Preparation**: UV-cured SiPSA was prepared using methyl vinyl MQ resin as the hard segment, methyl vinyl silicone rubber (110-2S) as the soft segment, and thiol silicone oil as the crosslinking agent. 2. **Performance Testing**: The effects of vinyl content in MQ resin, thiol/olefin molar ratio, and resin/rubber mass ratio on the performance of SiPSA were studied, including thermal stability, water resistance, mechanical properties, and adhesion properties. Through these studies, the authors hope to develop a new type of pressure-sensitive adhesive that is efficient, energy-saving, and suitable for thermally sensitive substrates or high-temperature environments.