Preparation and Application of a New Silicon-containing Acrylate Water Repellent
Fan YANG,Zhu WANG,Hai-feng LIU,Tao ZHANG,Tian-long LI
DOI: https://doi.org/10.11941/j.issn.1009-4369.2016.04.002
2016-01-01
Abstract:The cationic emulsion was synthesized with vinyl silicone oil , 3-[tris(trimethylsilyloxy)silyl] propyl methacrylate (TRIS), methyl methacrylate (MMA), butyl acrylate (BA) and acrylic acid (AA) as the main raw materials, cationic (OATAC) and nonionic (DNS500) compound as emulsifier, AIBA as initia-tor and GMA as cross -link agent , through the starved semi -continuous seed emulsion polymerization . Effects of type and proportion of complex emulsifier on the stability of the monomer pre -emulsion were dis-cussed.Effects of dosages of silicone , mass ration of Si(Tri) and TRIS, dosage of GMA, initiator and emulsi-fier on the gel rate , conversion rate and water repellency property were also discussed through the orthogonal test method .The obtained polymer emulsion was then characterized by IR spectroscopy , particle size , contact angle performance , spray test , transmission electron microscope and thermodynamic analysis .The results showed that the optimum synthesizing condition was obtained as follows:the dosage of organic silicon monomer was 25.0 wt%,mass ration of Si(Tri) and TRIS was 25/75, the dosage of GMA, emulsifier and initiator were 5 .0 wt%, 2 .7 wt%and 1 .4 wt%respectively .The polymer emulsion obtained under this condition showed-core/shell morphology obviously , and had excellent water repellent performance that the water contact angle was 114°,the oil contact angle was 64°, the surface energy was 15.4 mN/m, and the cotton fabric finished with this water repellent reached 90 points.