Abstract:A new type of waterborne polyurethane acrylate was synthesized for use as a UV curing coating. The N,N-dihydroxy methyl ethyl-3-Methyl aminopropanoate monomer was first prepared via adding reactions of methyl acrylate and diethanol amine with methyl alcohol as the solvent. Then, the hyperbranched prepolymer was obtained by addition of trimethylolpropane with toluenesulfonic acid as catalyst and N,N-dimethyl formamide as solvent. The resulting hyperbranched and organosilicone modified waterborne polyurethane acrylates was synthesized through the mixed reaction of prepolymer and Hydroxy silicone oil, polyethylene glycol-1000, toluene diisocynate, dimethylolpropionic acid, 1,2-propylene glycol, hydroxyethyl acrylate, and triethylamine with dibutyltin dilaurate as the catalyst. The molecular structures were characterized by FT-IR and 1H NMR spectroscopy and GPC analysis and the thermal stability was studied by using TGA. Moreover, the influence of contemodnt of hydroxyl silicone oil, dimethylolpropionic acid, polyethylene glycol-1000, and prepolymer to various of properties such as glossiness, hardness, adhesive force, abrasion resistance, water absorption, elongation at break and tensile strength of films were analyzed. The temperature and catalyst dosage impact on percent conversion of isocyanate group (–NCO) were also studied. It was proven that the best dosage of hydroxyl silicone oil and dimethylolpropionic acid were 4.6%, the dosage of polyethylene glycol-1000 was 50%, and the amount of hyperbranched prepolymer was 0.5%, which could make the film achieve the optimum properties. The percent conversion of isocyanate group (–NCO) was maximum when reacting two hours at 80 °C with 0.2% catalyst.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to improve the comprehensive performance of water - borne polyurethane acrylate (WPUA). Specifically, although the existing water - borne polyurethane acrylate is environmentally friendly, has good mechanical properties and compatibility, its water resistance, mechanical properties and optical properties are poor, and these shortcomings limit its wide application in various fields. Therefore, by introducing hyperbranched structures and silicone modification, this paper aims to synthesize a new type of hyperbranched silicone - modified water - borne polyurethane acrylate photosensitive resin to improve the performance of WPUA, making it have better water resistance, mechanical properties and optical properties.
To achieve this goal, the researchers carried out research in the following aspects:
1. **Synthesis of hyperbranched polymers**: Prepare N,N - dihydroxyethyl - 3 - aminopropionic acid methyl ester monomer through Michael addition reaction, and on this basis, use trimethylolpropane as the core molecule to synthesize hyperbranched polymers.
2. **Synthesis of hyperbranched silicone - modified water - borne polyurethane acrylate**: Mix and react the hyperbranched polymer with hydroxy silicone oil, polyethylene glycol - 1000, toluene diisocyanate, dimethylolpropionic acid, 1,2 - propanediol and other raw materials to prepare hyperbranched silicone - modified water - borne polyurethane acrylate.
3. **Performance testing**: Characterize the synthesized product by means of infrared spectroscopy (FT - IR), nuclear magnetic resonance (1H NMR), gel permeation chromatography (GPC), thermogravimetric analysis (TGA), etc., and test performance indicators such as the glossiness, hardness, adhesion, wear resistance, water absorption rate, tensile strength and elongation at break of the coating film.
The research results show that by optimizing the proportion of each component, especially when the amounts of hydroxy silicone oil and dimethylolpropionic acid are 4.6% respectively, the amount of polyethylene glycol - 1000 is 50%, and the amount of hyperbranched prepolymer is 0.5%, the coating film with the best performance can be obtained. In addition, the study also found that when the reaction is carried out at 80 °C for 2 hours and the amount of catalyst is 0.2%, the conversion rate of isocyanate group (- NCO) is the highest. These improvements make the synthesized resin have excellent thermal stability and good glossiness, thereby significantly improving the comprehensive performance of water - borne polyurethane acrylate.