Abstract:Abstract In this study, ureidopyrimidinone moieties (UPy), capable of physical crosslinking via quadruple hydrogen bonding, were successfully incorporated into UV-curable polyurethane acrylate prepolymers. First, a hydroxyl-terminated unsaturated ester monomer was synthesized and reacted with isophorone diisocyanate to create a hydroxyl-terminated UV-curable urethane oligomer (U–OH). Then, isocyanate-terminated building blocks (UPy moieties and an acrylate-based photosensitive monomer) were synthesized and used in various ratios to functionalize U–OH for the preparation of a series of UV-curable UPy-containing polyurethane acrylate (PUA) resins. The resulting products were structurally characterized using 1 H NMR and FTIR spectroscopy. Furthermore, organic–inorganic hybrid nanocomposites were obtained by introducing silane coupling agents into PUA resins using the sol–gel process. A series of UV-curable UPy-containing PUA coatings and hybrid nanocomposites were prepared, and their synergistic effect on coating properties was investigated. The dynamic mechanical analysis revealed that the Tg of the samples increased with increasing UPy content, although the mechanical properties remained largely unaltered, as shown by the stress–strain test. The studies also demonstrated that the hybrid nanocomposites exhibited higher decomposition temperatures and better thermal stability compared to pure PUAs. All the coatings exhibited good transparency in the visible region. An optical microscope was used to investigate the self-healing property by scratching the plexiglass panels with a razor blade. Among the other samples, the coating with the highest percentage of UPy content exhibited the best self-healing ability after heat treatment at 90 °C for 10 min. Graphical abstract

What problem does this paper attempt to address?

This paper mainly discusses how to prepare coating materials with self-healing ability and enhanced performance by introducing uracil-pyridone (UPy) groups into ultraviolet (UV) light-cured polyurethane acrylate (PUA) prepolymers. The researchers first synthesized an unsaturated ester monomer, which reacted with isophorone diisocyanate to produce hydroxyl-terminated UV-cured polyurethane oligomers (U-OH). Then, isocyanate-terminated building blocks containing UPy groups and acrylate-based photosensitive monomers were synthesized. These building blocks reacted with U-OH to prepare a series of UPy-containing PUA resins with different proportions. Silane coupling agents were introduced into the PUA resins via a sol-gel process to prepare organic-inorganic hybrid nanocomposites. The experimental results showed that with the increase of UPy content, the glass transition temperature (Tg) of the samples increased, but the mechanical properties remained basically unchanged. The hybrid nanocomposites exhibited higher decomposition temperature and better thermal stability. All coatings had good transparency in the visible light region. Microscopic observation revealed that the coating with the highest UPy content had the best self-healing ability after being treated at 90°C for 10 minutes. The paper also discussed how the physical crosslinking formed by UPy groups through quadruple hydrogen bonding could improve the mechanical and optical properties of the materials. A comparison with other studies indicated that introducing silane coupling agents through the sol-gel process could increase crosslink density and further enhance the performance of the coatings. In conclusion, this study aims to improve the heat resistance and self-healing characteristics of UV-cured coatings by synthesizing and characterizing UPy-containing PUA and its hybrid nanocomposites.

Synthesis and characterization of ureidopyrimidinone-functionalized polyurethane acrylates and their hybrid nanocomposites for UV coating applications