Abstract:Al-Cu alloy has broad application prospects in the field of aerospace due to its excellent performance. In this paper, deposits with different Cu contents were prepared by the wire arc additive manufacturing (WAAM) process, and the effects of Cu content on the microstructure and mechanical properties were investigated. The microstructure of Al-Cu alloy was investigated by metallography, scanning electron microscope (SEM), energy-dispersive spectrometer (EDS), and transmission electron microscope (TEM). The results show that both the number and size of the precipitated θ phases (Al2Cu) in the as-deposited material increase with the increase of Cu content. After the T4 treatment, the solid solution amount of Cu in the matrix showed a trend of first increasing and then remaining stable. When the content of Cu was greater than 5.65%, as the Cu content increased, the number and size of the remaining θ phases both increased. In the peak ageing state, the amount of precipitated θ’ phase showed a trend of increasing and then remaining stable. After the T6 treatment, the mechanical properties showed a trend of first increasing and then decreasing with the increase of the content of Cu. When the Cu content was 5.65%, the deposit achieved the best mechanical properties, and the anisotropy of the mechanical properties disappeared. The tensile strength, yield strength, and elongation reached 538 MPa, 478 MPa, and 10.5%, respectively. When the content of Cu was greater than 5.65%, the anisotropy of mechanical properties was obvious, and the fracture mode of the vertical specimen changed from ductile fracture to brittle fracture.

Preparation and properties of Al2O3 dispersed fine-grained W-Cu alloy

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Preparation and properties of W-30 wt% Cu alloy with the additions of Ni and Fe elements

Microstructure and Mechanical Properties of W-Al2O3 Alloy Plates Prepared by a Wet Chemical Method and Rolling Process

Excellent mechanical, thermal and electrical properties of ultrafine W-Cu alloys via freeze-drying technology

Nanostructured Composite Obtained by Mechanically Driven Reduction Reaction of Cuo and Al Powder Mixture

Sintering Densification of Cu/Al2O3p Nano-Composite Powders by Electroless Copper Plating

Synthesis and characterization of an in-situ Al2O3/Al–Cu composite with a heterogeneous structure

Development of Y2O3 Dispersion-Strengthened Copper Alloy by Sol-Gel Method

Synthesis, Characterization, and Dealloying of Al-Cu Alloys Prepared Using Spark Plasma Sintering

Effect of sintering temperature on fine-grained Cu W composites with high copper

Ultrahigh strength, thermal stability and high thermal conductivity in hierarchical nanostructured Cu-W alloy

Investigation on microstructure and properties of TiC0.5-Al2O3/Cu composites fabricated by a novel in-situ reactive synthesis

Effects of Sintering Temperature on the Microstructure and Properties of a W-Cu Pseudo-Alloy

Establishment of processing map, microstructure and high-temperature tensile properties of W-0.25 wt% Al2O3 alloys

Cu strengthened Al-Si-Cu semi-solid billet fabricated by liquid phase reaction sintering

Enhanced interfacial wettability and mechanical properties of Ni@Al2O3/Cu ceramic matrix composites using spark plasma sintering of Ni coated Al2O3 powders

Functionally Graded W-Cu Materials Prepared from Cu-Coated W Powders by Microwave Sintering

Preparation and microstructure of Cu-Al2O3 composites by a novel supercritical water liquid phase in-situ reaction method

Fabrication and microstructure of W-Cu composites prepared from Ag-coated Cu powders by electroless plating

The Effect of Cu Content on the Microstructure and Properties of the Wire Arc Additive Manufacturing Al-Cu Alloy