Effects of WC Particles on the Microstructure and Properties of Copper Matrix Composites by Selective Laser Melting
Kai Zhang,Weidong Liu,Weijun Liu,Binghan Li,Tianqing Ye,Huiru Wang,Hongyou Bian
DOI: https://doi.org/10.1016/j.jallcom.2024.177734
IF: 6.2
2024-01-01
Journal of Alloys and Compounds
Abstract:Selective Laser Melting (SLM), as an emerging additive manufacturing technology, has attracted increasing attention in the field of copper alloys. To reduce the production cost of SLM-formed copper alloys and enhance the mechanical properties of the alloy materials, this work uses CuSn10 alloy powder prepared by the water atomization method as the raw material, and optimizes the process parameters during SLM through the response surface and variance analysis methods, to prepare almost fully dense CuSn10 alloy blocks. By adding a certain proportion of WC hard particles to the CuSn10 alloy powder, this work investigates the microstructural evolution and mechanical properties of the specimens before and after the addition of particles, and explores the regularity of the influence of the addition of hard particles on the microstructural evolution and mechanical properties of the formed parts by comparing the experimental results. The results show that the SLM-formed CuSn10 specimens exhibit a fine-grained microstructure composed of cellular and dendritic structures. The addition of WC hard particles changes the microstructure of the composite material, eliminating the preferred growth inside the specimens, and due to the effects of hard carbide phase, heterogeneous nucleation and dispersion strengthening, a more refined and uniform microstructure is achieved. The performance of the specimens also varies considerably, with the Vickers hardness increasing from 155HV to 215HV, the ultimate tensile strength increasing from 578MPa to 625MPa, and the elongation at fracture decreasing from 15% to 5%. The wear resistance and corrosion resistance show the same trend, with the wear resistance and corrosion resistance of the composite material first decreasing and then increasing as the WC content increases, reaching the best when the content is 10%. It can be seen that by reasonably adjusting the proportion of the WC reinforcement phase in the copper-based composite material, the hardness and wear resistance of the SLM-formed CuSn10 alloy can be significantly improved, expanding the engineering application prospects of copper alloy parts in extreme working conditions such as wear and corrosion.