Abstract:Nanocrystalline pure perovskite phase bismuth sodium titanate (Bi0.5Na0.5)TiO3(BNT) powders have been prepared by a sol-gel method from the poly vinyl alcohol evaporation route. bismuth nitrate [Bi(NO3)(3)], tetra-butyl titanate [Ti(OC4H9)(4)] and sodium acetate(CH3COONa) were used as raw materials and poly vinyl alcohol(PVA) as the sol-gel forming solvent. Stoichiometric amounts of the individual raw materials were thoroughly mixed in accordance with the BNT composition to form the stock solution. The pH of the stock was adjusted to 1-3 by adding acetate. Aqueous solution of PVA[10%(w/v)] was then added to the cationic mixture with thorough stirring. The weight ratio of the cationic mixture to the PVA aqueous solution was maintained at 2:1. The resulting viscous liquid was then heated over a hot crucible up to form a fluffy dry gel. The fluffy dry gels were calcined at different temperatures and times and then cooled to room temperature naturally. The X-ray powder diffraction(XRD) patterns of the heat-treated powders were obtained using a Bruker D8 Advance X-ray diffractometer with Cu K alpha radiation and nickel filter. Scanning electron microscope (SEM) studies of the NBT powders were performed using a JSM-6700F electron microscope. Phase-pure BNT powders were obtained at 550 degrees C for 2-2.5h which is relatively lower calcination temperature than other reports. The BNT powders consists of phase-pure perovskite nanocrystals with an average size of 100-200nm.

Low temperature preparation of NaTi2(PO4)3 by sol-gel method

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Sol-Gel Preparation of N-doped TiO2 Nanocrystalline at Low Temperature

Synthesis of Perovskite Structure (Ca-0.61, Nd-0.26)TiO3 Nanopaticles by Sol-Gel Method

Preparation of Ti1-xFexO2 Nanocrystals via Low Temperature Sol-Gel Method

LOW-TEMPERATURE PREPARATION OF NANO-CRYSTALLINE LITHIUM NIOBATE POWDERS BY THE POLYMERIC PRECURSOR METHOD

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Sol-Gel Synthesis and Characterization of Nanocrystalline (bi0.5na0.5)tio3 Powders from the Poly Vinyl Alcohol Evaporation Route

Preparation and Dielectric Properties of (ca0.61,nd0.26)tio3 Nanoparticles by a Sol–gel Method

Low Temperature Synthesis of Vanadium Pentoxide Nanocrystallines by Sol-Gel Method

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

pH control on preparation of nano-TiO_2 by gel-sol process

Low-temperature Synthesis of Bi4Ti3O12 Nanocrystals by Hydrothermal Method

Low-temperature Synthesis of Nano-Crystalline Magnesium Titanate Materials by the Sol–gel Method

Preparation of Single-Crystalline BaTi5O11 Nanocrystals by Hydrothermal Method

Preparation And Characterization Of Nano-Yb2o3/Tio2 Particles

Monodisperse Hollow Perovskite BaTiO3 Nanostructures Prepared by a Sol–gel–hydrothermal Method

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches

Preparation of (NaBi)(1/2)TiO3 piezoelectric ceramic powder by sol-gel process

Synthesis and characterization of Bi1/2Na1/2TiO3 nanopowders by pyrogenation-with-sugar-protection method