Abstract:High-temperature superconductor (Re)Ba2Cu3Ox (ReBCO) conductor on round core cable (CORC®) has a large current carrying capacity for high field magnets. Lorentz forces acting on CORC conductors, cause a reduction of the critical current, or even permanent degradation of their performance when exceeding critical values. Transverse compressive stress is one of the principal mechanical stresses when CORC cables are bundled to CICC conductors capable of operating at currents up to 100 kA in magnetic fields of up to 20 T. In this research, a mechanical-electromagnetic model is developed to study the effect of transverse compressive loads on the electromagnetic performance of CORC cables. A mechanical transverse load on the cable is implemented to simulate the electromagnetic force. A comparison of numerical simulations with experiments for a three-layer CORC cable is first performed to validate the model's reliability, with particular attention to critical current reduction during the transverse compression process. A novel feature of this paper is that the model developed can analyze both mechanical response under transverse compressive loads and electromagnetic performance under applied AC magnetic fields with low amplitudes. On this basis, the model investigates the effects of winding parameters on the axial strain and critical current reduction of the ReBCO layer in a single-layer CORC cable. The numerical analysis shows that increasing the winding angle can reduce the axial strain and critical current reduction of the ReBCO layer in the contact area. Subsequently, a detailed comparative study is carried out studying the axial strain of the ReBCO layer in the non-contact area with and without taking the winding core into account. In addition, a sudden increase of the magnetization loss is explained when the transverse compressive load reaches a certain level. Finally, a six-layer CORC cable's electromagnetic analysis is performed, and each tape layer's critical current reduction is investigated and discussed. The comparison of magnetization loss and current density between six- and single-layer CORC cables in the no-strain case is also given. This FE model can guide optimizing a cable design for specific application conditions.

Impact of Anticlastic Deformation on REBCO Tapes Wound in Multilayer Round Cable

Experimental Study on Cabling Properties of Different REBCO Coated Tapes

Electromechanical degradation of REBCO coated conductor tapes under combined tension and torsion loading

Performance study of REBCO multi-filament tapes/ CORC cables prepared by reel-to-reel mechanical incision

Characterization of a novel TORT cable wound of stabilized striated REBCO tapes for reduced magnetization AC losses

Analyses of the plastic deformation of coated conductors deconstructed from ultra-high field test coils

Experimental Study on the Critical Current of CORC Cable under Cyclic Bending-straightening

Optimization of REBCO Tapes through Division and Striation for Use in Superconducting Cables with Low AC Losses

Experimental Study on Critical Current of Bent ReBCO Tapes in CORC Type Cable

Critical Current Degradation Behaviour of Various REBCO Tapes under Uniaxial Strain

Performance Degradation of Multi-Layer Spiral Cable During Manufacturing Procedure

Effect of the Cu Stabilisation Layer on the Turn-to-turn Contact Resistance of a Non-Insulated REBCO Winding

Critical current degradation and delamination crack observation of epoxy-coated REBCO superconducting tapes after thermal cycles in liquid nitrogen

Novel Two-Step Procedure for Measuring I C Vs. Tensile Stress of Commercial REBCO Tape

Plastic Deformation Simulation of REBCO Tapes Using Particle Methods

The current unbalance in stacked REBCO tapes -- simulations based on a circuit grid model

Bending-Peeling Method to Research the Effect of Lateral Stress on Superconductivity of REBCO Tape at Liquid-Nitrogen Temperature

Investigating the effect of transverse compressive loads on the electromagnetic performance of superconducting CORC® cables

Evaluation of the effect of edge cracks on critical current degradation in REBCO tapes under tensile stress

Current Sharing in Superconducting REBCO Cables-FEM Modeling

Current-carrying properties of REBCO multi-filamentary tapes prepared by reel-to-reel ultraviolet picosecond laser cutting