Current-carrying properties of REBCO multi-filamentary tapes prepared by reel-to-reel ultraviolet picosecond laser cutting
Zuoguang Li,Zhan Zhang,Yuhu Bu,Donghu Wang,Guanyu Xiao,Huan Jin,Jinggang Qin,Chao Zhou
DOI: https://doi.org/10.1088/1361-6668/ad80d6
2024-09-28
Superconductor Science and Technology
Abstract:REBCO high-temperature superconductor has been widely used in high magnetic field applications, because of the excellent critical current properties and high critical temperature. However, REBCO tape has an extremely large width-to-thickness ratio (typically in the range of 1000-10000) to cause too high power dissipation in the applications. One of the effective ways to reduce AC loss is to divide the superconducting layer in the REBCO tape into filaments. The current-carrying properties degradation behavior of the prepared multi-filamentary tape is the focus of attention. In this study, REBCO multi-filamentary tapes with different numbers of filaments (2-filament, 6-filament, and 10-filament) by cutting the copper-stabilizing layers and superconducting layers through a self-developed reel-to-reel ultraviolet picosecond laser cutting device. The findings indicate that the cut groove has a depth of approximately 30 μm and the width of the groove on the superconducting layer measures around 15 μm. Meanwhile, the researchers found that ultraviolet picosecond laser cutting does not cause substantial degradation in the IC. Under self-field conditions at 77 K, the IC decreases with the number of filaments, and the degradation of IC is less than 13% in a 10-filament tape, the corresponding decrease of JC is only about 10%. Similarly, at 4.2 K and under various high-field (10 T, 12 T, 14 T) conditions, the IC variation trends of REBCO HTS multi-filamentary tapes and non-striated tapes are fundamentally similar, both decreasing as the applied vertical magnetic field increases. Furthermore, it was found that a constant tension of 50 MPa, 100 MPa, and 200 MPa had no effect on the current-carrying properties of the REBCO HTS multi-filamentary tapes.
physics, condensed matter, applied