Fatigue failure mechanism of Ti60 titanium alloy in HCF and VHCF regime at different temperatures

Chao-Lin Chen,De-Guang Shang,Zhi-Qiang Tang,Dao-Hang Li,Xiang Yin,Yi-Er Guo

DOI: https://doi.org/10.1016/j.engfailanal.2023.107393

IF: 4

2023-06-08

Engineering Failure Analysis

Abstract:The failure mechanism of Ti60 titanium alloy in the high cycle fatigue (HCF) and very high cycle fatigue (VHCF) at different temperatures was investigated. The results showed that, at different temperatures, there are two different fatigue failure mechanisms, i.e., the oversized facet and oxide shedding failure mechanisms. At room temperature, most of the fatigue cracks initiate at the oversized facet. At 300°C, the crack initiates at the oversized facet for the test with small applied stress, while the crack initiates at the oxide shedding site for the test with large applied stress. At 400°C, all the fatigue cracks initiate at the oxide shedding site. Higher temperature and stress will be conducive to the failure mechanism of oxide shedding to become dominant.

engineering, mechanical,materials science, characterization & testing