Abstract:<p>The damage mechanisms and load redistribution taking place under high temperature (350°C), high cycle fatigue (HCF) of TC17 titanium alloy/unidirectional SiC fibre composites have been investigated <em>in situ</em> using synchrotron X-ray computed tomography (CT) and X-ray diffraction (XRD) under two stress amplitudes. The three-dimensional morphology of the fatigue crack and fibre fractures has been mapped by CT. At low stress amplitude, stable growth occurs with matrix cracking deflecting by 50-100 µm in height as it bypasses the bridging fibres. At higher stress amplitude, loading to the peak stress led to a burst of fibre fractures giving rise to rapid crack growth. Many of the fibre fractures occurred 50-300 µm above/below the matrix crack plane during rapid growth, contrary to that in the stable growth stage, leading to extensive fibre pull-out on the fracture surface. The changes in fibre loading, interfacial stress, and the extent of fibre-matrix debonding in the vicinity of the crack have been mapped over the fatigue cycle and after the rapid growth by XRD. The fibre/matrix interfacial sliding extends up to 600 µm (in the stable-growth zone) or 700 µm (in the rapid-growth zone) either side of the crack plane. The direction of interfacial shear stress reverses over the loading cycle, with the maximum frictional sliding stress reaching ∼55 MPa in both regimes. In accordance with previous studies, it is possible that a degradation in fibre strength at elevated temperature is responsible for bursts of fibre fracture and rapid crack growth under higher stress amplitude.</p>

Fracture mechanism of Ti60 alloy at high temperature in very high cycle fatigue regime and fatigue life prediction

Fatigue failure mechanism of Ti60 titanium alloy in HCF and VHCF regime at different temperatures

Fatigue life prediction of Ti60 titanium alloy under very high cycle loading at different temperatures

Crack Initiation Mechanism and Life Prediction of Ti60 Titanium Alloy Considering Stress Ratios Effect in Very High Cycle Fatigue Regime

Fatigue cracking behavior and life assessment of TC11 titanium alloy in very high cycle regime at two working temperatures

Microstructure based cracking behavior and life assessment of titanium alloy under very-high-cycle fatigue with elevated temperatures

Very high cycle fatigue behavior of laser powder bed fusion additively manufactured Ti6Al4V alloy at elevated temperature

Microstructural effects on the high-cycle fatigue and fracture behaviors of Ti-6Al-4V alloy

Crack initiation mechanism of titanium alloy in very high cycle fatigue regime at 400°C considering stress ratio effect

Life Prediction and Failure Analysis in Laser Powder Bed Fused TiC/Ti6Al4V Titanium Matrix Composite under High Cycle and Very High Cycle Fatigue Conditions

High‐cycle and very‐high‐cycle fatigue behavior and life prediction of Ni‐based superalloy at elevated temperature

Fracture Criterion for Predicting Surface Cracking of Ti40 Alloy in Hot Forming Processes

Titanium Alloy Materials with Very High Cycle Fatigue: A Review

Fatigue behavior and fracture characteristics of 718Plus nickel-based superalloy at high temperature

Effect of thermal exposure on the microstructure and mechanical properties of Ti60 alloy

High fatigue performance and microscopic mechanisms of in-situ TiB 2 /7050Al composite at different temperatures

Damage accumulation during high temperature fatigue of Ti/SiCf metal matrix composites under different stress amplitudes

Dwell and Normal Cyclic Fatigue Behaviours of Ti60 Alloy

Damage accumulation during high temperature fatigue of Ti/SiC$_f$ metal matrix composites under different stress amplitudes

Very high cycle fatigue of a nickel-based superalloy at room and elevated temperatures: Interior failure behavior and life prediction

Effect of Stress Ratio on Very High Cycle Fatigue Properties of Ti-10V-2Fe-3Al Alloy with Duplex Microstructure