Abstract:In this study, the mechanism of thermal exposure on the mechanical properties of two Ti60 alloys with different micro-texture regions (MTRs) was systematically investigated through macro- and microstructural characterization. It was found that when the alloy was exposed to prolonged thermal exposure at 600 °C for 100 h, the strength of the no-MTR samples increased significantly and the plasticity decreased sharply. In contrast, the MTR samples showed a sharp decrease in strength and plasticity due to the transmissibility of dislocation slip and crack propagation, resulting in the formation of a continuous brittle cleavage plane on the fracture. Meanwhile, the oxide film formed on the surface promotes the formation of early cracks and cleavage planes, and the oxide film serves as the location of surface crack nuclei and creates a notch effect leading to premature fracture of the alloy. It is further found that the oxide film is mainly composed of alternating nanocrystalline grains of Al 2 O 3 and TiO 2 , and there is an oxygen-rich layer of Ti 3 O near the matrix, and these nano-oxides increased the brittleness of the oxide film. The strengthening and embrittlement mechanism of the alloy was revealed based on the deformation characteristics, i.e. the plasticity reduction was attributed to the formation of the oxide film and precipitation of the α 2 phase on the surface, whereas the inhomogeneous distribution of the α 2 phase in the interior led to the formation of microcracks in the interior. The precipitation of (Ti, Zr) 6 Si 3 phase at grain boundaries hinders the dislocation motion and leads to a significant increase in the strength of No-MTR alloys. This study reveals the effects of interactions between MTRs, oxide films and precipitated phases on the thermal exposure properties of Ti60 alloys, providing theoretical support for the stability of titanium alloy properties at elevated temperatures.

Effect of thermal exposure on the microstructure and mechanical properties of Ti60 alloy

The effect of heat treatment system on mechanical properties of titanium alloy BTi-6554

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Microstructural Evolution and Subsequent Mechanical Properties of Ti65 Titanium Alloy during Long-Term Thermal Exposure

Effects of Thermal Exposure Temperature on Room-Temperature Tensile Properties of Ti65 Alloy

Effect of Thermal Exposure on Microstructure Evolution and Mechanical Properties of TC25G Alloy

The Effect of Thermal Exposure on the Microstructures and Mechanical Properties of 2198 Al–Li Alloy

Mechanism of thermal exposure on the mechanical properties of microtextured Ti60 alloys

Thermal stability and its effects on the mechanical properties of rapidly solidified Al-Ti alloys

Microstructure and Sliding Wear Behavior of PM Alloy Al10Ti after Thermal Exposure

Microstructural effects on the high-cycle fatigue and fracture behaviors of Ti-6Al-4V alloy

Influence of thermal exposure on the microstructure evolution and mechanical behaviors of an Al-Cu-Li alloy

Influence of thermal exposure on microstructural stability and tensile properties of a new Ni-base superalloy

Effect of Solution Temperature on Microstructure and Mechanical Properties of Ti–5Al5Mo5V3Cr1Zr Alloy

Effect of Thermal Exposure on the Microstructure and Mechanical Properties of 2A97 Al-Li Alloy

Impact of Heat Treatment on the Mechanical Properties and Fracture Morphology of Ti555211 Alloy

Investigation on the microstructure evolution and dynamic recrystallization mechanisms of TiAl alloy at elevated temperature

High fatigue performance and microscopic mechanisms of in-situ TiB 2 /7050Al composite at different temperatures

Effect of Aging Temperature on the Microstructure and Mechanical Properties of a Novel β Titanium Alloy

Response of tribological behaviors to microstructural characteristics of Ti-40Al-10V alloy at high temperatures

Effects of different heat treatment temperatures on the microstructure and mechanical properties of additive manufacturing Ti65 alloys