Effect of Annealing Temperature on the Strength and Toughness of Ti‐55531 Titanium Alloy After Multiple Heat Treatment
Lei Zhang,Jiangxiong Wang,Mingpan Wan,Chaowen Huang,Min Lei,Rui Ma,Dan Liu,Xianli Ren,Tianxin Li
DOI: https://doi.org/10.1002/adem.202400953
IF: 3.6
2024-09-21
Advanced Engineering Materials
Abstract:Herein, the effects of annealing temperature on the microstructure and mechanical properties of Ti‐55531 alloy under the multiple heat treatment of "solution + annealing + aging" are investigated. Results, the annealing temperature changes the size distribution of αs, changing the crack propagation mode and fracture mechanism, the strength and plasticity are more matched. Herein, it is aimed to reveal the effect of annealing temperature on α microstructure parameters and mechanical properties of Ti‐55531 alloy under the multiple heat‐treatment process of "solution (855 °C) + annealing (700, 730, 760 °C) + aging (600 °C)." The microstructure is characterized by using optical microscopy, scanning electron microscopy, and transmission electron microscope. In the results, it is indicated that the annealing temperature does not change the volume fraction of the αs phase of Ti‐55531 alloy. The as‐annealed precipitation‐free zone αs phase renucleates after aging treatment, resulting in a bimodal distribution of αs phase in the matrix. The higher the annealing temperature, the larger the average size of αs phase and the greater the heterogeneity in the alloy. Additionally, the heterogeneity of αs phase affects further the plasticity and the crack propagation path of the alloy. With the increase of annealing temperature, the strength of Ti‐55531 alloy decreases slowly, but the elongation and the impact toughness of the alloy increases rapidly resulting from the heterogeneity of αs phase under multiple heat‐treatment conditions.
materials science, multidisciplinary