Abstract:Ti6Al4V (Ti64) alloys manufactured by selective laser melting (SLM) are well known for their susceptibility to failure at a low ductility of less than 10% due to the formation of an (α′) martensitic structure. Annealing and solution treatments as post-heat treatments of α′ are considered a good way to improve the mechanical performance of SLM-manufactured Ti64 parts. In this research, the effect of heat treatment parameters such as temperature (850 °C and 1020 °C) and cooling rate (furnace and water cooling) on the microstructure and mechanical properties of the SLM Ti64 structure was investigated. It was shown that the tensile strength/ductility of the Ti64 alloy produced by SLM was determined by the post-heat treatment. The experimental results revealed that heat treatment at 850 °C followed by furnace cooling resulted in the best possible combination of ductility (13%) and tensile strength (σy = 932, σu = 986 MPa) with a microstructure consisting mainly of 78.71% α and 21.29% β. Heat treatment at 850 °C followed by water cooling was characterized by a reduction in hardness and the formation of predominantly α plus α′′ and a small amount of β. HT850WC exhibited yield and tensile strengths of about 870 and 930 MPa, respectively, and an elongation at fracture of 10.4%. Heat treatment at 1020 °C and subsequent cooling in the furnace was characterized by the formation of an α + β lamellar microstructure. In contrast, heat treatment at 1020 °C and subsequent water cooling formed semi-equiaxial β grains of about 170 μm in diameter with longer elongated α grains and basket-weave α′. Post-treatment at 1020 °C followed by furnace cooling showed high ductility with an elongation of 14.5% but low tensile strength (σy = 748, σu = 833 MPa). In contrast, post-treatment at 1020 °C followed by water cooling showed poor ductility with elongation of 8.6% but high tensile strength (σy = 878, σu = 990 MPa). The effect of aging at 550 °C for 3 h and cooling in a furnace on the microstructure and mechanical properties of the specimens cooled with water was also studied. It was found that aging influenced the microstructure of the Ti6Al4V parts, including β, α, and α′′ precipitation and fragmentation or globularization of elongated α grains. The aging process at 550 °C leads to an increase in tensile strength and a decrease in ductility.

The Effect of Annealing and Cryogenic Treatment on the Microstructure and Mechanical Properties of Ti-6Al-4V Alloy

The effect of heat treatment system on mechanical properties of titanium alloy BTi-6554

Effect of Annealing Temperature on As-Cast Ti6Al4V–5Cu Alloy Microstructure, Tensile Properties, and Fracture Toughness

Effect of Annealing Temperature on the Strength and Toughness of Ti‐55531 Titanium Alloy After Multiple Heat Treatment

High strength and toughness of Ti–6Al–4V sheets via cryorolling and short-period annealing

Achieving synergistic improvement of wear and mechanical properties in Ti–6Al–4V alloy by multiple cryogenic treatment

Effects of Different Heat Treatments on Microstructure and Mechanical Properties of TC4-DT Titanium Alloy Bar

Annealing microstructure evolution and strength-plasticity enhancement mechanism of a novel titanium alloy Ti6422

Effects of Annealing and Solution Treatments on the Microstructure and Mechanical Properties of Ti6Al4V Manufactured by Selective Laser Melting

Microstructure and Mechanical Properties of Ti62421S High Temperature Titanium Alloy with Different Heat Treatments

The Influence of Deep Cryogenic Treatment (DCT) on the Microstructure Evolution and Mechanical Properties of TC4 Titanium Alloy

Simultaneously enhancing strength and ductility of Ti-6Al-4V alloy with the hierarchical structure via a novel thermal annealing treatment

Study on the Performance Improvement of Titanium Alloy through Deep Cryogenic and Thermal-cold Cycling Treatment

Effects of cryogenic treatments on phase transformations, microstructure and mechanical properties of near βTi alloy

Effect of Heat Treatment on the Microstructure and Mechanical Properties of Additive Manufactured Ti-6.5Al-2Zr-1Mo-1V Alloy

Effect of Aging Treatment on Microstructural Evolution and Mechanical Properties of the Electron Beam Cold Hearth Melting Ti-6Al-4V Alloy

Effect of annealing treatment on microstructure and tensile properties of Ti-48Al-2Cr-5Nb alloy fabricated by laser additive manufacturing

Exploring the Heat Treatment Parameters, Microstructural Evolution, and Mechanical Properties of Ti–6Al–4V Alloy Fabricated by a Selective Laser Melting Process

Effect of Annealing on the Microstructure, Texture, and Properties of Cold-Rolled Ti50Ni47Fe3 Shape Memory Alloy Sheets

Microstructural evolution and mechanical properties of selective laser melted Ti-6Al-4V induced by annealing treatment

Effect of Novel Thermomechanical Treatment on Microstructure and Properties of 6156 Alloy