Abstract:As technology has developed along with the increasing mechanical demands placed upon it, the need for fatigue exceeding 107 cycles or even longer for machines and components is necessary, not only for safety and reliability, but also for minimizing the economic and human costs brought about by failure. Titanium alloys have been one of the most widely used and most important materials in the aerospace domain owing to their superior properties of high strength-weight ratio and good temperature resistance. Studies have shown that S-N curves of TC4 alloy exhibit a linearly decreasing tendency and no fatigue limit around 107 cycles under very highcycle fatigue. Thus, fatigue strength design according to the traditional standard is adventurous to some extent. In this study, an electromagnetic resonant fatigue testing machine at a frequency of 100 Hz was employed to carry out fatigue tests and investigate the influence of two stress ratios (R = 0. 1 and-1) on TC4 titanium alloy under a very high-cycle fatigue regime. The results show that S-N curves under each of the two stress ratios present the so called"duplex characteristic"while their respective failure mechanisms are different. The fracture of specimens under R = 0. 1 corresponds to two modes, i. e., surface failure induced by machining defects, and interior fisheye failure, accompanied by the appearance of facets. The horizontal part of the S-N curve at stress ratio of 0. 1 represents the transition stress between the surface failure and the interior failure, beyond which the surface failure can take place, while surface failure without facets only occurs under R =-1. Based on fracture mechanics, the threshold value of small crack growth is lower under a positive stress ratio and in a vacuum, which is more conducive to crack propagation and formation of facets. From these results, the interior fatigue failure process and mechanism of TC4 titanium can be explained as follows: (1) the appearance of slip lines or bands inpartial α grain; (2) initiation and coalescence of micro-crack; (3) formation of granular bright facets (GBF); (4) formation of fisheye; (5) unstable crack propagation outside the fisheye; (6) instantaneous fracture.

Crack initiation mechanism of titanium alloy in very high cycle fatigue regime at 400°C considering stress ratio effect

Fatigue Voids and Sub-Grain Boundaries Assisted Crack Initiation with High Stress Ratio in Vhcf Regime for Titanium Alloy at 400℃

Creep-fatigue Voids and Sub-Grain Boundaries Assisted Crack Initiation for Titanium Alloy in VHCF Regime with High Mean Stress at 400°C

Crack Initiation Mechanism in a High-Strength Ti-5Al-7.5V Alloy Subjected to High Cycle Fatigue Loading

Fatigue failure mechanism of Ti60 titanium alloy in HCF and VHCF regime at different temperatures

Crack Initiation and Early Growth Behavior of TC4 Titanium Alloy under High Cycle Fatigue and Very High Cycle Fatigue

Crystallographic Micro-Mechanism of Faceted Crack Initiation in Near-Α Titanium Alloy Ti6321 under Room-Temperature Fatigue and Dwell Fatigue Loadings

The mechanism of internal fatigue-crack initiation and early growth in a titanium alloy with lamellar and equiaxed microstructure

Fatigue Crack-Initiation Mechanisms of a Dual-Phase Titanium Alloy Exhibiting High Tensile and High-Cycle Fatigue Properties

Microstructure-based Interior Cracking Behavior of Α + Β Titanium Alloy under Two Stress Ratios and Intermediate Temperature in the Very High-Cycle Fatigue Regime

Fatigue cracking behavior and life assessment of TC11 titanium alloy in very high cycle regime at two working temperatures

Crack Initiation Mechanisms under Two Stress Ratios Up to Very-High-cycle Fatigue Regime for a Selective Laser Melted Ti-6Al-4V

Characteristic and mechanism of crack initiation and early growth of an additively manufactured Ti-6Al-4V in very high cycle fatigue regime

Crack Initiation Mechanism and Life Prediction of Ti60 Titanium Alloy Considering Stress Ratios Effect in Very High Cycle Fatigue Regime

Cyclic Deformation and Microcrack Initiation During Stress Controlled High Cycle Fatigue of a Titanium Alloy

Low Cycle Fatigue Behavior and Crack Initiation Mechanism of Ni-based Single Crystal Curved Thin-Walled Blade Simulator Specimen with Film Cooling Holes

Effect of Stress Ratio on Very High Cycle Fatigue Properties of Ti-10V-2Fe-3Al Alloy with Duplex Microstructure

Microstructure based cracking behavior and life assessment of titanium alloy under very-high-cycle fatigue with elevated temperatures

Initiation and Early-Stage Growth of Internal Fatigue Cracking under Very-High-Cycle Fatigue Regime at High Temperature

Crack initiation mechanisms of micro-textured Ti60 alloys with different dwell sensitivities subjected to fatigue and dwell fatigue loading

Effect of Stress Ratio on the Very High-Cycle Fatigue Failure Mechanism of TC4 Titanium Alloy