Abstract:Fatigue crack initiation mechanism at high cycle regime in a bimodal Ti-5Al-7.5V alloy are investigated by fracture observations, focused-ion-beam cross-section and electron back-scattered diffraction characterizations. The aged Ti-5Al-7.5V exhibits superior tensile and fatigue properties, alongside a wide range of fatigue life when tested at the stress levels of - 700-800 MPa. Fatigue failure was dominated by surface and subsurface crack initiation at facets matching basal planes. These faceted primary alpha (alpha p) grains generally have a medium or high Schmid factor (SF) for basal < a > slip. Moreover, a basal faceting process also occurred in the "hard" grains, in which the c-axis of the HCP-alpha grains was approximately parallel to the loading axis so that the < a > type slips were thought to be suppressed. The observed internal microcracks were formed along the grain boundaries located in clusters of alpha p grains, especially along (0001) twist boundaries. Furthermore, transmission electron microscope observations evidenced the absence of intense slip bands within faceted grain and fatigued alpha p grains, which indicates that the facet growth should not along the pre-existing slip bands resulting from high cycle fatigue loadings. The pre-existing structural defects including dislocation networks and subgrain boundaries within alpha p grains are relatively stable configurations under fatigue loadings. The observed fine (-500 nm in diameter) silicides were widely dispersed, whether the silicide can act as the crack nucleation site still needs further more detailed studies and this remains an open question.

Fatigue life prediction of Ti60 titanium alloy under very high cycle loading at different temperatures

Fatigue cracking behavior and life assessment of TC11 titanium alloy in very high cycle regime at two working temperatures

Microstructure based cracking behavior and life assessment of titanium alloy under very-high-cycle fatigue with elevated temperatures

Crack Initiation Mechanism and Life Prediction of Ti60 Titanium Alloy Considering Stress Ratios Effect in Very High Cycle Fatigue Regime

Fracture mechanism of Ti60 alloy at high temperature in very high cycle fatigue regime and fatigue life prediction

Fatigue failure mechanism of Ti60 titanium alloy in HCF and VHCF regime at different temperatures

Prediction of Fatigue Life of TC4 Titanium Alloy Based on Normalized Equivalent Initial Flaw Size Model

A novel very-high-cycle-fatigue life prediction model with interior microstructure induced cracking behavior of Inconel-713C superalloy at 25 °C, 750 °C and 1000 °C

High‐cycle and very‐high‐cycle fatigue behavior and life prediction of Ni‐based superalloy at elevated temperature

Very high cycle fatigue of a nickel-based superalloy at room and elevated temperatures: Interior failure behavior and life prediction

High-temperature fatigue behavior of TC17 titanium alloy and influence of surface oxidation

The Low-Cycle Fatigue Behavior, Microstructure Evolution, and Life Prediction of SS304: Influence of Temperature

Low Cycle Fatigue Behavior of Original Ferritic P92 Steel at High Temperature: Experiments and Simulations

Life prediction method based on damage mechanism for titanium alloy TC4 under multiaxial thermo-mechanical fatigue loading

Fatigue Crack-Initiation Mechanisms of a Dual-Phase Titanium Alloy Exhibiting High Tensile and High-Cycle Fatigue Properties

Lifetime prediction of time-dependent thermomechanical fatigue of high temperature alloys

Fatigue life modeling for a low alloy steel after long-term thermal aging

HIGH TEMPERATURE CREEP AND FATIGUE BEHAVIOR AND LIFE PREDICTION METHOD OF A TiAl ALLOY

High Temperature Low Cycle Fatigue Properties and Failure Mechanism of a TiAl Alloy

Effect of elevated temperature on high-cycle and very-high-cycle fatigue properties of Ni-based superalloy manufactured by selective laser melting

Crack Initiation Mechanism in a High-Strength Ti-5Al-7.5V Alloy Subjected to High Cycle Fatigue Loading