MC decomposition and boride formation in a next generation polycrystalline Ni based superalloy during isothermal exposure at 900 °C

H.S. Kitaguchi,L. Small,I.P. Jones,Y.L. Chiu,M.C. Hardy,P. Bowen

DOI: https://doi.org/10.1016/j.matchar.2024.113721

IF: 4.537

2024-02-08

Materials Characterization

Abstract:Detailed microstructural characterisation of phases present in a next generation polycrystalline Ni based superalloy after thermal exposure at 900 °C was carried out, focusing on carbides and borides. Metastable M 5 B 3 precipitated after 32 h had a stoichiometry of (Cr 0.7 Mo 0.2 W 0.1 ) 5 B 3 with substitutions with Ni, Co, Nb and Ta. Fine M 23 C 6 (a = 10.62 Å) was overgrown by metastable M 5 B 3 , as shown by rigorous TEM-SAD pattern investigation. The borides were eventually dominated by Mo rich M 3 B 2 , at the apparent expense of MC. Decomposition of MC was confirmed; it transformed sequentially to γ and then γ ́. The primary driving force for the MC decomposition was attributed to γ ́ precipitation, increasing its fraction to the thermodynamic equilibrium at 900 °C.

materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing