Abstract:Mechanical behaviors of a Ni-based single crystal superalloy have been investigated by tensile testing at various temperatures. Deformation substructures and mechanisms have been systemically revealed from micrometer to atomic scales by using advanced scanning electron and scanning transmission electron microscopes. Results show that deformation mode of the alloy strongly depends on the temperature due to competitive responses of the gamma and gamma' phases under mechanical loading and their original stress statuses. At temperatures from ambient to 750 degrees C, plasticity is governed by dislocation shearing in both phases, where slip modes of gamma are < 110 >{111} and those of gamma' are < 112 >{111}, < 110 >{111} and < 110 > {001}. At moderate temperatures (850 degrees C <= T <= 900 degrees C), plasticity mainly involves microscopically uniform deformation of both phases. The matrix deforms first so that channels parallel to tensile direction are narrowed due to the Poisson's effect, after that deformation of gamma' follows. The active slip modes are < 110 > {111} for gamma, < 112 >{111}, < 110 >{111}, < 110 >{001}, and < 001 >{001} for gamma'. At temperature higher than 1000 degrees C, plastic strain is also derived from deformation of both phases, but deformation of the matrix plays critical roles, due to relatively weak strength of this phase. The operative slip modes are < 110 > {111} for gamma, but mainly < 110 >{001} and < 001 >{001} for gamma'. Our results clearly provide a comprehensive and multiscale (from micrometer to atomic) understanding on the deformation mechanism of Ni-based superalloys, which can be critically beneficial and offer mechanistic guidelines to design new/next generation superalloys. (c) 2021 Elsevier Ltd. All rights reserved.

B1914 Ni-Based Superalloy Properties After Solution Heat Treatment and Long-Term Exposure at High Temperature

B22-P-17Evolution of the MC Carbide in Nickel-base Single Crystal Superalloy Exposing at 950 °C

Influence of thermal exposure on microstructural stability and tensile properties of a new Ni-base superalloy

Effects of Heat Treatment on the Microstructure and Properties of a Cast Nickel-Based High-Cr Superalloy

The microstructure evolution and its effect on the mechanical properties of a hot-corrosion resistant Ni-based superalloy during long-term thermal exposure

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

The Mechanical Properties of Intermetallic Ni50−xTi50Alx Alloys (X=6,7,8,9)

Microstructure and Elevated Temperature Tensile Behaviour of Directionally Solidified Nickel Based Superalloy

Microstructure evolution of a nickel‐based powder metallurgy superalloy under different solution treatment temperatures

Microstructural Evolution of a High W Content Ni-Based Superalloy at γ′ Sub-Solvus Temperatures

Effect of Heat Treatment on the Microstructure and Fracture Behaviors of a Ni–Cr–Fe Superalloy

Influence of Heat Treatment on Microstructure and Stress Rupture Property of Nickel-base Superalloy

Gamma prime and TCP phases and mechanical properties of thermally exposed nickel-base superalloy

Effect of Heat Treatment Temperature on Microstructure, Tensile Properties and δ-Precipitate Phase in Ni-based Superalloy

Microstructure Evolution and Mechanical Properties of High Nb-TiAl Intermetallic Compounds during Heat Treatment

Microstructure Evolution and Mechanical Properties of NiAlCrFeMo High Entropy Superalloy after Different Annealing Treatment

MC decomposition and boride formation in a next generation polycrystalline Ni based superalloy during isothermal exposure at 900 °C

High-Temperature Tensile Strength of Al10Co25Cr8Fe15Ni36Ti6 Compositionally Complex Alloy (High-Entropy Alloy)

Isothermal short‐term oxidation behavior of MAR‐M246 nickel‐based superalloy at 800°C and 1000°C

Microstructural homogenization and high-temperature cyclic oxidation behavior of a Ni-based superalloy with high-Cr content

Effect of Microstructural Evolution and Mechanical Properties of Haynes 230 Superalloy During Long-Term Aging at 700 °C