Microstructure Evolution and Mechanical Performance of Nickel Based Superalloy C1023 at Elevated Temperatures
Yahui Liu,Jun Wang,Maodong Kang,Feifei Mao,Jianzhong Li,Guoxiang Wang,Shuxian He,Haiyan Gao,Baode Sun
DOI: https://doi.org/10.1016/j.matchar.2018.01.048
IF: 4.537
2018-01-01
Materials Characterization
Abstract:Microstructure evolution of polycrystalline nickel based superalloy C1023 casting was investigated by corn paring as cast superalloy and heat treated superalloy in the paper. Influences of strengtheners and carbides on the tensile behaviors of heat treated superalloy at different temperatures (20 degrees C, 650 degrees C, and 850 degrees C) were studied. Resulting data from deep corrosion suggested that growth mode of scripted carbide included nucleation on the vertex of blocky carbonitride, expansion of dendrite arm in C-rich area, and enlargement of dendrite cap. Decomposition of MC carbide generated numerous octahedral M23C6 carbide as well as nanoscale Cr-Mo-rich nuclei. Diffusion of Mo from gamma to precipitates such as MC, and M23C6, occurred during the heat treatment while irregular gamma' (4 nm-500 nm) transformed into cuboidal particles. At 650 degrees C, no significant deterioration of tensile strength was found while plastic deformation ability of gamma base was improved. Oxidation of grain boundaries (GBs) dominated the crack behavior of the superalloy at 850 degrees C.