Microstructure evolution of a nickel‐based powder metallurgy superalloy under different solution treatment temperatures

Yuanyuan Zhang,Jikang Li,You Wu,Qingshuai Feng,Jiantao Liu,Tong Liu
DOI: https://doi.org/10.1002/adem.202200004
IF: 3.6
2022-04-26
Advanced Engineering Materials
Abstract:The effects of solution treatment temperature from 1120 to 1220 °C on the microstructure of a new nickel‐based powder metallurgy superalloy have been systematically studied. As the solution temperature increased from 1120 to 1160 °C, the grains of γ matrix grew slowly due to the pinning of primary γ' phase. With the solution of γ' phase and carbides between 1160 and 1180 °C, the γ grains enlarged quickly from 6.7 to 32.1 μm, whereas the grain growth slowed down from 1180 to 1220 °C owing to the decrease of interface energy of grain boundaries. The grain growth model has been established, and the activation energy of grain growth was calculated to be 298.5 KJ/mol. After solution treatment above 1170 °C, both the primary γ' precipitates at the prior particle cores (PPCs) and prior particle boundaries (PPBs) dissolved completely. The size of secondary γ' precipitates increased linearly with solution temperature, while the size of MC carbides changed slightly. The hardness variation of the samples under different solution temperatures were mainly due to the combined effects of grain size and the size of γ' precipitates.This article is protected by copyright. All rights reserved.
materials science, multidisciplinary
What problem does this paper attempt to address?