Synthesis of lithium conducting titanium phosphates by the sol-gel process

A. Guillot,D. Giaume,A. Suvorova,M. N. Rager,J.-B. d’Espinose de Lacaillerie,C. Mir,X. Randrema,P. Barboux

DOI: https://doi.org/10.1007/s10971-024-06461-2

2024-06-23

Journal of Sol-Gel Science and Technology

Abstract:The synthesis of titanium and lithium phosphates was studied using the sol-gel method. Particular attention was paid to phosphate precursors, which were mixtures of phosphate mono- and diesters prepared by solvolysis of P 4 O 10 in isopropanol. The reaction of these precursors with titanium and lithium alkoxides yielded homogeneous gels and after drying and thermal cleavage of the esters at 300 °C, amorphous inorganic products. For the composition corresponding to the stoichiometric formula of a stable compound such as LiTi 2 (PO 4 ) 3 , the phase crystallized as early as 550 °C by nucleation from the amorphous mixture. Ionic conductivity measured at room temperature was of the order of 10 −5 S·cm −1 which increased after heat treatment at higher temperatures. If the composition did not correspond to a stable thermodynamic phase, phase separation occurred, and ionic conductivity decreased between 500 °C and 700 °C.

materials science, ceramics