Solid State Reaction Synthesis and Characterization of Lithium Lanthanum Titanate Lithium-Ion Conducting Solid Electrolyte with Different Li to La Content

Andrew Dono,Rinlee Butch M. Cervera,Rinlee Butch Cervera

DOI: https://doi.org/10.4028/www.scientific.net/KEM.821.389

2019-11-25

Key Engineering Materials

Abstract:Lithium Lanthanum Titanate, Li 3 x La (2/3)- x □ (1/3)-2 x TiO 3 , with three different compositions of (i) x = 0.097 (Li 0.29 La 0.57 TiO 3 ), (ii) x = 0.117 (Li 0.35 La 0.55 TiO 3 ), and (iii) x = 0.167 (Li 0.50 La 0.50 TiO 3 ) were prepared via solid state reaction synthesis sintered at 1150 °C for 36 hours. X-ray diffraction (XRD) analysis revealed that all samples can be indexed to a cubic perovskite structure with lattice parameter a of about 3.86 Å. Morphological analysis using SEM showed that the samples are relatively dense and the calculated relative density of the LLTO samples range from about 94% to as high as 99% with increasing trend as Li content increases. Room temperature conductivity and its temperature dependence up to 120 °C were investigated. LLTO sample with x =0.117 revealed the highest total ionic conductivity at room temperature of about 1.69 x 10 -03 S/cm which can be a promising solid electrolyte for an all-solid-state lithium-ion batteries.