Preparation and Evaluation of High Lithium Ion Conductivity Li1.3al0.3ti1.7(Po4)(3) Solid Electrolyte Obtained Using A New Solution Method

Furui Ma,Erqing Zhao,Shaoyin Zhu,Wenchao Yan,Deye Sun,Yongcheng Jin,Cewen Nan

DOI: https://doi.org/10.1016/j.ssi.2016.07.010

IF: 3.699

2016-01-01

Solid State Ionics

Abstract:A NASICON-type (Na ion super conductor) structured Li1.3Al0.3Ti1.7(PO4)3 (LATP) solid electrolyte with high lithium ion conductivity was synthesized using a simple solution method with 85% H3PO4 solution. In comparison with conventional solid-state reaction and sol-gel method, the pure LATP powders and dense LATP pellets were obtained at a relatively lower temperature. The LATP powders and the resultant pellets were characterized by X-ray diffraction, scanning electron microscopy (SEM) and AC impedance spectroscopy. The LATP pellet obtained at 800°C for 12h shows the highest total conductivity of 1.21×10−3Scm−1 at room temperature and the lowest activation energy of 0.26eV. These results imply that the LATP electrolytes obtained using this method can be considered as candidates for solid state electrolytes.