Abstract:A new, simple, and highly efficient heating technology for metal tape substrates is proposed and applied to reel-to-reel and double-sided film deposition. In this technology, direct electrical current (I DC) is conducted into the metal layer of oxide-buffered metal substrate to induce heat. Different substrate surface temperatures were achieved by varying I DC from 22 to 25 A. At these temperatures, a series of 1-μm-thick and 5-cm-long YBa2Cu3O7−δ (YBCO) films were fabricated on ion-beam-assisted deposition (IBAD) templates through metal organic chemical vapor deposition. X-ray diffraction analysis on the samples revealed that the YBCO film changed its growth mode from mixed a-axis and c-axis to purely c-axis with increasing I DC. The optimal out-of-plane and in-plane texture reached ~1.4° and 3.5°, respectively. A 30-m-long and 500-nm-thick single-sided YBCO-coated conductor was also prepared through reel-to-reel deposition using the proposed heating method. The fabricated conductor presented homogeneous crystallization and texture and exhibited a critical current density at self-field and 77 K (J c 77K, 0T ) of 2.8–3.2 MA/cm2. Moreover, 500-nm-thick YBCO films were fabricated simultaneously on both sides of the double-sided IBAD template. The two sides of films demonstrated uniform texture and J c 77K, 0T of 3.2 MA/cm2. Results demonstrated that the proposed substrate heating technology can be used for reel-to-reel and double-sided deposition of YBCO-coated conductors.

Metalorganic Deposition of YBCO Films for Second-Generation High-Temperature Superconductor Wires

Thick $\Hbox{yba}_{2}\hbox{cu}_{3}\hbox{o}_{7-\Delta}$ Superconducting Films by Low-Fluorine Metallorganic Solution Deposition

MOD-Derived YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ</sub> Thin Films using a Fast Pyrolysis Process

Production of Long YBCO-coated Conductors using the TFA-MOD Method

Exfoliated YBCO filaments for second-generation superconducting cable

Mod-derived YBa2Cu3O7-δ thin filmsusing a fast pyrolysis process

High-Performance YBCO-Coated Superconductor Wires

Surface Morphology and Profile Analysis for Five-Layer YBa 2 Cu 3 O 7− Δ Thick Films Prepared by Low-Fluorine Metallorganic Deposition

Low-cost YBCO coated conductor technology

A review of the ion beam assisted deposition researches towards industrialization for the second generation high temperature superconducting wire fabrication

Effects of BaCO3 in transient liquid-assisted fluorine-free metal organic deposition on the growth process of YBCO

PREPARATION AND PROPERTIES OF Ba-MO SOURCE FOR MOCVD

Property Improvement of 600-Nm-thick YBCO Superconducting Films Fabricated Using a Pb-Modified MOD Method

Theoretical Analyses of Chemical Solution Deposition Derived YBCO Thick Film Assisted by a High Magnetic Field

Self-heating Technique of Metallic Substrate for Reel-to-reel and Double-Sided Deposition of YBa 2 Cu 3 O 7− Δ Films

Advance in Long-Length REBCO Coated Conductors Prepared by Reel-to-Reel Metalorganic Solution and Ion-Beam-Assisted Deposition

Fabrication and Analysis of Tri-layer YBaCu Thick Films by Low-Fluorine MOD Method

Fabrication and Analysis of Tri-layer YBa 2 Cu 3 O 7− δ Thick Films by Low-Fluorine MOD Method

Development of High Critical Current YBCO Coated Conductors by Photo-Assisted MOCVD

Cost-effective and High-Rate Process for Solution-Drived YBa<inf>2</inf>Cu<inf>3</inf>O<inf>7-&#x03B4;</inf> Coated Conductors

Preparation of Double-Sided MgO Template for YB2Cu3O7-δ Coated Conductors