Abstract:In this paper, methods for the prevention of voids in local Al-BSF PERC solar cells are discussed. The thermodynamics of the formation of local contacts is analyzed. It is shown that reducing the diffusivity and the driving force of Si diffusion into the Al layer are critical factors in void prevention. Two new firing profiles have been designed to overcome the void issue. The first firing process is a two-step procedure. The solar cells are initially heated to a low temperature (for example, 650°C, depending on the melting point of Al paste) allowing some silicon to diffuse into the aluminum layer. The firing temperature is then ramped up to the peak firing temperature. This method is compatible with the co-firing process of the front Ag paste. The void ratio is reduced from 52% (the baseline) to 8%, and the average efficiency of PERC solar cells is improved by an absolute 0.09%. The second proposed firing process is an extension of the first one and consists of a multi-step procedure. As in the first approach, the solar cells are heated at a low temperature (depending on the melting point of Al paste) for a long enough time for the silicon concentration in aluminum to saturate. The temperature is then gradually ramped up. For each step increase in temperature, there is enough time for the silicon concentration to saturate. With this technique, the void ratio can be reduced to nearly 0%. The optimization of the second approach is not yet finalized due to co-firing compatibility issues with the front Ag electrodes. Together with other processes improvements, in pilot production, the local Al-BSF PERC cells have achieved an average efficiency of 19.91% and an independently-measured champion efficiency of 20.54%.

Improvement of Laser Contact Opening in Bifacial PERC Solar Cells by Optimizing the Dashed Pattern

Performance optimization of PERC solar cells based on laser ablation forming local contact on the rear

Improvement of Light Trapping in Bifacial PERC Silicon Solar Cells by Optimizing the Rear Surface Morphology

Improved Bifacial Properties of P‐Type Passivated Emitter and Rear Cell Solar Cells toward High Mass Production Efficiency

Optimization of rear surface roughness and metal grid design in industrial bifacial PERC solar cells

Effect of back opening ratio and layout design on the performance of laser ablated point contact cell

Influence of laser condition on the electrical and mechanical performance of bifacial half‐cutting PERC solar cell and module

Bifacial p-Type PERC Solar Cell with Efficiency over 22% Using Laser Doped Selective Emitter

Optimization of Rear-Side Passivation for Enhancing the Performance of Bifacial PERC+ Solar Cells

Improvement of Laser-Induced Damage on High-Efficiency Solar Cells via Top-Hat Beam Ablation

Passivated Emitter and Rear Cell Silicon Solar Cells with a Front Polysilicon Passivating Contacted Selective Emitter

Recombination Behaviour of Passivated Emitter and Rear Cell (PERC) Bifacial Silicon Solar Module under Different Illuminations

Effective Way to Reduce Rear-Side Potential-Induced Degradation of Bifacial PERC Solar Cells

Preventing the Formation of Voids in the Rear Local Contact Areas for Industrial-Type PERC Solar Cells

Effect of Rear Pyramid Structures on Industrial Bifacial PERCs under Omnidirectional Incidence

Pathway towards 24% efficiency for fully screen-printed passivated emitter and rear contact solar cells

Light management of PERC solar cell with the front and back dielectric multilayers

Tailoring Interdigitated Back Contacts for High-performance Bifacial Silicon Solar Cells

Qualitative Damage Assessment of Laser Contact Opening and Microstructural Evolution at the Rear Contact of a Perc Mono Crystalline Si Solar Cell upon Co-Firing with Si Doped Al Paste

Optimization of Controllable Factors in the Aluminum Silicon Eutectic Paste and Rear Silicon Nitride Mono-Passivation Layer of PERC Solar Cells

Ultrathin Bifacial Passivated Emitter and Rear Cell with Inverted Pyramid Textures