Abstract:LECO technology plays an important role for reducing the J0,metal and ρc. First, LECO paste destroys the partial passivation layer but does not corrode downward at low sintering temperature; then after LECO treatment, the glass layer was melting and continued to further corrode the ARC layer without damaging the emitter layer, forming localized corrosion pits. The contact model shows that its possible current transport mechanism is current tunneling effect through the nano‐Ag colloids in the glass layer. TOPCon solar cell with boron (B)‐doped emitters plays an important role in photovoltaic cell technology. However, a major challenge to further improving the metallization‐induced recombination and electrical contact of B‐doped emitters. Laser‐enhanced contact optimization (LECO) technology is one of ideal candidates for reducing the metallization recombination and contact resistivity. In this study, we investigate the influence of LECO technology using special Ag paste with a decreased Pb content on the performance of the metallization‐induced recombination (J0,metal), contact resistivity (ρc), microtopography of the contact, the I–V parameters, and possible conductive mechanisms. The results showed that the linear resistivity is reduced from 3.56 to 2.60 μΩ·cm owing to special Ag paste, and after LECO treatment, it also has lower ρc about 0.91 mohm·cm2. Both of them have a large contribution to the FF enhancement. Meanwhile, the J0,metal drops from 500 to 200 fA/cm2, which provides a great contribution to the improvement in open‐circuit voltage. The efficiency improved by 0.26% absolute to 25.94%, mainly because of the increased open‐circuit voltage (Voc) of 4 mV and a fill factor (FF) of 0.26%. Simulated by COMSOL, the electron concentration rises to 4 × 1019 cm−3 after LECO treatment, which can generate a larger reverse current to provide a melting temperature for the glass frit, increasing the interface glass phase conductivity. The possible current transport mechanism of LECO is current tunneling effect, resulting in the decrease in the metallization recombination. After the optimization of the LECO process with low‐corrosion paste, we manufactured industrial‐grade TOPCon cells with Eff, Voc, Jsc, and FF values as high as 26.5%, 736 mV, 42.1 mA/cm2, and 85.5%, respectively.

Effect of back opening ratio and layout design on the performance of laser ablated point contact cell

Improvement of Laser Contact Opening in Bifacial PERC Solar Cells by Optimizing the Dashed Pattern

Performance optimization of PERC solar cells based on laser ablation forming local contact on the rear

Improvement of Laser-Induced Damage on High-Efficiency Solar Cells via Top-Hat Beam Ablation

Silicon heterojunction back contact solar cells by laser patterning

Qualitative Damage Assessment of Laser Contact Opening and Microstructural Evolution at the Rear Contact of a Perc Mono Crystalline Si Solar Cell upon Co-Firing with Si Doped Al Paste

Optimizing the Back Contact of Kesterites and Perovskites: Band Edge Design and Defect Engineering in Molybdenum Chalcogenides

Multi-physics Coupling Effects of Nanostructure Characteristics on the All-Back-contact Silicon Solar Cell Performances

Effect of the Back Surface Topography on the Efficiency in Silicon Solar Cells

Investigation on Effects of the Laser‐Enhanced Contact Optimization Process With Ag Paste in a Boron Emitter for n‐TOPCon Solar Cell

A Simulation Study of the Micro-Grooved Electrode Structure for Back-Contact Back-Junction Silicon Solar Cell

Influence of laser condition on the electrical and mechanical performance of bifacial half‐cutting PERC solar cell and module

Performance of Large Area n-TOPCon Solar Cells with Selective Poly-Si Based Passivating Contacts Prepared by PECVD Method

Reducing the stress concentration of back contact solar cells: Optimizing the process of drilling

Study on the influence of micro-alkali texturing and micro-alkali polishing process on the passivation and contact performance of n-TOPCon solar cells

Optimization of Shunt Isolation Processing for Silicon Solar Cells Via Laser and Chemical Etching

Investigation of Laser Doping and Plating Process for Cost-Effective PV Metallization

An insight into effect of front surface field on the performance of interdigitated back contact silicon heterojunction solar cells

Performance Optimization by Considering Current Matching in Polymer Tandem Solar Cells

Enhancing the reliability of TOPCon technology by laser-enhanced contact firing

Microstructural Passivation of Patterned Al2O3 Back Contacts on CdS/CdTe Solar Cells