Abstract:Effective capture of radioiodine is crucial for the sustainable development of nuclear power, given its environmental mobility, high toxicity, and long half-life. Herein, a new core–shell structured Bi 2 S 3 derived from ZIF-8 was synthesized by cation exchange, sulfation and carbonization. The advantage of this structure is that Bi 2 S 3 uniformly loads on the surface of nanoparticles, effectively avoiding its aggregation and improving the utilization of active sites. The iodine capture experiments indicated that Bi 2 S 3 had excellent adsorption capacity (up to 1118.5 mg g −1 within 120 min) and high chemisorption percentage (87.3 %) at 200 °C, as well as superior thermal and irradiation stability. The mechanism investigations revealed that the exceptional iodine uptake performance was predominantly attributed to the strong chemical reaction between Bi 2 S 3 and I 2 to generate BiI 3 . Additionally, the iodine-captured Bi 2 S 3 could be immobilized in a commercial glass composition via low-temperature sintering. The findings indicated that the captured BiI 3 and I 2 were efficiently converted to the chemically stable Bi x O y I during the sintering process. The initial leaching rate of iodine was 3.94 × 10 −5 g m −2 d −1 , which signified the excellent chemical durability of the resultant glass composites. Therefore, the obtained Bi 2 S 3 could be a promising candidate for efficient capture and stable storage of radioiodine.

High Retention Immobilization of Iodine in B-Bi-Zn Oxide Glass Using Bi 2 O 3 as a Stabilizer under a N 2 Atmosphere

High Retention Immobilization of Iodine in B-Bi-Zn Oxide Glass Using Bi2O3 As a Stabilizer under a N2 Atmosphere

Immobilization of Iodine Waste Forms: A Low-Sintering Temperature with Bi2O3-B2O3-ZnO Glass

Low-sintering-temperature borosilicate glass to immobilize silver-coated silica-gel with different iodine loadings

Role of amorphous silica gel in B2O3-Bi2O3-ZnO-SiO2 to immobilize iodine waste

Bi2O3 doped B2O3-ZnO glass powder for immobilization of radioactive iodine waste at low temperature

Immobilization of iodine waste at low sintering temperature: Phase evolution and microstructure transformation

The immobilization on various concentrations of iodine in silver-coated silica gel via B2O3–Bi2O3 based material

B2O3–Bi2O3–ZnO based materials for low-sintering temperature immobilization of iodine adsorbed waste

Synthesis of glass composite material with bismuthate glass powder and zeolite-4A for immobilization of iodine waste

Utilization of B 2 O 3 –Bi 2 O 3 –ZnO low-temperature glass-ceramics to immobilize iodine-loaded silver-coated silica-gel

Bismuth Coordinates with Iodine Atoms to Form Chemical Bonds for Existing Stabilization in Boron Glass

Low-temperature fabrication of glass-based iodine waste forms via a novel preparation method

Sintering Bi2O3–B2O3–ZnO Ternary Low Temperature Glass by Hydration Device to Solidify Iodine Containing Silver-Coated Silica Gel

Performance research and engineering application of B2O3-Bi2O3-ZnO glass powder for solidifying iodine-containing silver silica gel

Immobilization of iodine waste via the gas-pressure sintering of glass-bonded iodosodalite ceramic

Core-shell structured Bi 2 S 3 -ZnS@C derived from ZIF-8 for efficient capture and reliable storage of volatile radioactive iodine

Direct Immobilization of Iodine-Loaded Silver-Coated Silica Gel with Silicate Glass Powders at Low Temperature

Application of silica gel to immobilise iodine waste by low-temperature sintering

Novel Method for Efficient Solidification the Iodine Contained Waste by B2O3–Bi2O3 Glass Powder at Very Low Temperature

Immobilization of silver-coated silica gel with varying iodine loading in silicate glass ceramics