Synthesis of glass composite material with bismuthate glass powder and zeolite-4A for immobilization of iodine waste

Yi Liu,Yaxin Feng,Guilin Wei,Runjie Sun,Xirui Lu,Yan Chen,Lin Peng,Meihua Ma,Yu Zhang,Zhentao Zhang

DOI: https://doi.org/10.1016/j.jssc.2020.121856

IF: 3.3

2021-02-01

Journal of Solid State Chemistry

Abstract:<p>The immobilization of iodine 129 released during the reprocessing of spent nuclear fuels has attracted increasing interest in the field of nuclear waste management. Glass composite materials have been developed to decrease the sintering temperature considering the iodine volatilization. In this study, the effects of the addition (5–25 ​wt%) of a bismuthate oxide glass powder and sintering temperature (500–1100 ​°C) on the iodosodalite formation in waste forms were investigated. Microstructure characterization techniques including X-ray diffraction, scanning electron microscopy, energy-dispersive spectroscopy, and X-ray photoelectron spectroscopy were employed to elucidate the I states in the waste form. Phase composition calculations show that the maximum phase mass of iodosodalite was 94%. The sintering temperature was decreased to 600 ​°C, lower than the decomposition temperature of NaI, after the addition of a 15 ​wt% bismuthate glass powder. The leaching rate of iodine shows the considerable chemical durabilities of the sintered sample under alkaline and neutral conditions.</p>

chemistry, physical, inorganic & nuclear

What problem does this paper attempt to address?

The paper primarily explores the method of using bismuth-containing glass powder and zeolite 4A to synthesize glass composites for immobilizing iodine waste (particularly radioactive iodine-129). The core objective of the study is to reduce the synthesis temperature to minimize iodine volatilization and improve immobilization efficiency.

Specifically, the authors investigated the effect of adding different proportions (5-25 wt%) of bismuthate glass powder to a mixture of sodium iodide (simulated radioactive iodine waste) and zeolite 4A. By adjusting the sintering temperature (500-1100°C), they evaluated the impact of these conditions on the immobilization of sodium iodide into iodosodalite. Iodosodalite is a substance with a β-cage structure that can effectively accommodate iodine atoms and iodate ions.

The results showed that when 15 wt% of bismuthate glass powder was added and sintered at 600°C, the formation of iodosodalite was maximized, reaching a mass fraction of 94%. This temperature is below the decomposition temperature of sodium iodide (approximately 670°C), indicating that this method can effectively immobilize iodine at a lower temperature.

Additionally, chemical stability tests were conducted, and the results showed that the leaching rate of iodine was very low under alkaline and neutral conditions, demonstrating the good chemical stability of the prepared materials. These findings suggest that glass composites containing bismuth glass powder are an effective material for iodine waste immobilization.

In summary, the paper aims to develop a new method for iodine waste immobilization. By controlling the sintering conditions and adding an appropriate amount of bismuthate glass powder, the synthesis temperature was successfully reduced, and the immobilization efficiency of iodine was improved.