Core-shell structured Bi 2 S 3 -ZnS@C derived from ZIF-8 for efficient capture and reliable storage of volatile radioactive iodine

Kai-wei Chen,Ao-tian Gu,Xin-yu Zhou,Peng Wang,Chun-hui Gong,Ping Mao,Yan Jiao,Kai Chen,Yi Yang

DOI: https://doi.org/10.1016/j.seppur.2023.124380

IF: 8.6

2023-06-23

Separation and Purification Technology

Abstract:Effective capture of radioiodine is crucial for the sustainable development of nuclear power, given its environmental mobility, high toxicity, and long half-life. Herein, a new core–shell structured Bi 2 S 3 derived from ZIF-8 was synthesized by cation exchange, sulfation and carbonization. The advantage of this structure is that Bi 2 S 3 uniformly loads on the surface of nanoparticles, effectively avoiding its aggregation and improving the utilization of active sites. The iodine capture experiments indicated that Bi 2 S 3 had excellent adsorption capacity (up to 1118.5 mg g −1 within 120 min) and high chemisorption percentage (87.3 %) at 200 °C, as well as superior thermal and irradiation stability. The mechanism investigations revealed that the exceptional iodine uptake performance was predominantly attributed to the strong chemical reaction between Bi 2 S 3 and I 2 to generate BiI 3 . Additionally, the iodine-captured Bi 2 S 3 could be immobilized in a commercial glass composition via low-temperature sintering. The findings indicated that the captured BiI 3 and I 2 were efficiently converted to the chemically stable Bi x O y I during the sintering process. The initial leaching rate of iodine was 3.94 × 10 −5 g m −2 d −1 , which signified the excellent chemical durability of the resultant glass composites. Therefore, the obtained Bi 2 S 3 could be a promising candidate for efficient capture and stable storage of radioiodine.

engineering, chemical