Abstract:This work introduces a stack layer of Lithium Phosphate (Li3PO4) /Titanium Dioxide (TiO2) as a new electron selective passivating contact for c‐Si solar cells. The stack achieves an impressive contact resistivity (ρc) of 0.128 mΩ cm2 on n‐type c‐Si substrates with resistivity ranging from 1 to 3 Ω cm2. Furthermore, it effectively reduces the surface recombination parameter (J0) to less than 4 fA by incorporating a 6 nm a‐Si:H(i) layer. Carrier selective contacts with passivation effects are considered to have a significant influence on the performance of crystalline silicon (c‐Si) solar cells. It is essential for electron selective contact materials to meet the requirements of ultra‐low contact resistance and excellent passivation effects. This work introduces a stack layer of Lithium Phosphate (Li3PO4) /Titanium Dioxide (TiO2) as a new electron selective passivating contact. It is found that the stack achieves an impressive contact resistivity (ρc) of 0.128 mΩ cm2 on n‐type c‐Si substrates with resistivity ranging from 1 to 3 Ω cm (14.6 mΩ cm2 for the n‐Si/a‐Si:H/Li3PO4/TiO2/Al contact). Furthermore, it effectively reduces the surface recombination parameter (J0) to less than 4 fA by incorporating a 6 nm a‐Si:H(i) layer. The characterization of the n‐Si/Li3PO4/TiO2 interface reveals that phosphorus diffusion into silicon plays a crucial role in achieving the ultra‐low contact resistivity, while the presence of PO43− groups helps in fixing hydrogen atoms to maintain the desired chemical passivation effect. Finally, a silicon heterojunction solar cell (SHJ) with a rear full‐area configuration of a‐Si:H/Li3PO4/TiO2/Al is successfully demonstrated achieving an impressive power conversion efficiency of 22.89%. The result proves the efficacy of employing hydrogen‐rich low‐work function metal oxide stacks as electron selective passivating contacts.

Novel interlayer boosting the performance of evaporated Cu2O hole‐selective contacts in Si solar cells

Interfacial Engineering of Cu 2 O Passivating Contact for Efficient Crystalline Silicon Solar Cells with an Al 2 O 3 Passivation Layer

Improved V 2 O X Passivating Contact for p ‐Type Crystalline Silicon Solar Cells by Oxygen Vacancy Modulation with a SiO X Tunnel Layer

Effective Hydrogenation Strategies to Boost Efficiency over 20% for Crystalline Silicon Solar Cell with Al2O3/Cu2O Passivating Contact

Chromium Trioxide Hole-Selective Heterocontacts for Silicon Solar Cells

Titanium Dioxide Hole-Blocking Layer in Ultra-Thin-Film Crystalline Silicon Solar Cells

Solution-Processed Copper (I) Iodide via Co-Doping for Enhanced Hole Selective Contacts in P-Type Crystalline Silicon Solar Cells

Full-Area i-a-Si:H/ATO/Mg Electron-Selective Contacts for Silicon Solar Cells

Self‐Diffusion Effect Assisted TiO2/Li3PO4 Electron Selective Passivating Contact in Silicon Solar Cells Approaching 23% Efficiency

Design and Optimization of SiOx/AZO Transparent Passivating Contacts for High‐Efficiency Crystalline Silicon Solar Cells

Copper-Plating Metallization With Alternative Seed Layers for c-Si Solar Cells Embedding Carrier-Selective Passivating Contacts

High‐Performance and Industrially Viable Nanostructured SiO x Layers for Interface Passivation in Thin Film Solar Cells

Enhancement of NiOx/poly‐Si Contact Performance by Insertion of an Ultrathin Metallic Ni Interlayer

Principles of dopant-free electron-selective contacts based on tunnel oxide/low work-function metal stacks and their applications in heterojunction solar cells

Thermal optimization of defected Cu2O photon-absorbing layer and the steady p-Cu2O/n-Si photovoltaic application

A novel silver-doped nickel oxide hole-selective contact for crystalline silicon heterojunction solar cells

Electron‐Selective Strontium Oxide Contact for Crystalline Silicon Solar Cells with High Fill Factor

Sn‐doped Nb2O5 films as effective hole‐selective passivating contacts for crystalline silicon solar cells

A silicon carbide-based highly transparent passivating contact for crystalline silicon solar cells approaching efficiencies of 24%

Efficient Silicon Solar Cells with Aluminum‐Doped Zinc Oxide‐Based Passivating Contact

Thermally stable MoOx hole selective contact with Al2O3 interlayer for industrial size silicon solar cells