Abstract:This work introduces a stack layer of Lithium Phosphate (Li3PO4) /Titanium Dioxide (TiO2) as a new electron selective passivating contact for c‐Si solar cells. The stack achieves an impressive contact resistivity (ρc) of 0.128 mΩ cm2 on n‐type c‐Si substrates with resistivity ranging from 1 to 3 Ω cm2. Furthermore, it effectively reduces the surface recombination parameter (J0) to less than 4 fA by incorporating a 6 nm a‐Si:H(i) layer. Carrier selective contacts with passivation effects are considered to have a significant influence on the performance of crystalline silicon (c‐Si) solar cells. It is essential for electron selective contact materials to meet the requirements of ultra‐low contact resistance and excellent passivation effects. This work introduces a stack layer of Lithium Phosphate (Li3PO4) /Titanium Dioxide (TiO2) as a new electron selective passivating contact. It is found that the stack achieves an impressive contact resistivity (ρc) of 0.128 mΩ cm2 on n‐type c‐Si substrates with resistivity ranging from 1 to 3 Ω cm (14.6 mΩ cm2 for the n‐Si/a‐Si:H/Li3PO4/TiO2/Al contact). Furthermore, it effectively reduces the surface recombination parameter (J0) to less than 4 fA by incorporating a 6 nm a‐Si:H(i) layer. The characterization of the n‐Si/Li3PO4/TiO2 interface reveals that phosphorus diffusion into silicon plays a crucial role in achieving the ultra‐low contact resistivity, while the presence of PO43− groups helps in fixing hydrogen atoms to maintain the desired chemical passivation effect. Finally, a silicon heterojunction solar cell (SHJ) with a rear full‐area configuration of a‐Si:H/Li3PO4/TiO2/Al is successfully demonstrated achieving an impressive power conversion efficiency of 22.89%. The result proves the efficacy of employing hydrogen‐rich low‐work function metal oxide stacks as electron selective passivating contacts.

Self‐Diffusion Effect Assisted TiO2/Li3PO4 Electron Selective Passivating Contact in Silicon Solar Cells Approaching 23% Efficiency

21.3%-Efficient N-Type Silicon Solar Cell with a Full Area Rear TiOx/LiF/Al Electron-Selective Contact

TiO2 Films from the Low-Temperature Oxidation of Ti as Passivating-Contact Layers for Si Heterojunction Solar Cells

Effective Hydrogenation Strategies to Boost Efficiency over 20% for Crystalline Silicon Solar Cell with Al2O3/Cu2O Passivating Contact

Approaching 23% Efficient N-Type Crystalline Silicon Solar Cells with a Silicon Oxide-Based Highly Transparent Passivating Contact

Dual Functional Dopant-Free Contacts with Titanium Protecting Layer: Boosting Stability while Balancing Electron Transport and Recombination Losses

Interfacial Engineering of Cu 2 O Passivating Contact for Efficient Crystalline Silicon Solar Cells with an Al 2 O 3 Passivation Layer

Design and Optimization of SiOx/AZO Transparent Passivating Contacts for High‐Efficiency Crystalline Silicon Solar Cells

A High-Quality Dopant-Free Electron-Selective Passivating Contact Made from Ultra-Low Concentration Water Solution

Solution‐Processed Electron‐Selective Contacts Enabling 21.8% Efficiency Crystalline Silicon Solar Cells

Full-Area i-a-Si:H/ATO/Mg Electron-Selective Contacts for Silicon Solar Cells

Pinhole-like Carriers Transport in Spin-Coating SiO2 Enabling High-Efficiency Dopant-Free Si Solar Cells

Electron‐Selective Contacts ATO/LiF/Al‐Based High‐Performance N‐Type Silicon Solar Cells

Stable Dopant-Free Electron-Selective Contact for Silicon Solar Cells

Efficient Silicon Solar Cells with Aluminum‐Doped Zinc Oxide‐Based Passivating Contact

Enhancing poly-Si contact through a highly conductive and ultra-thin TiN layer for high-efficiency passivating contact silicon solar cells

One‐Step Formation of Low Work‐Function, Transparent and Conductive MgFxOy Electron Extraction for Silicon Solar Cells

Polysilicon Passivating Contacts for Silicon Solar Cells: Interface Passivation and Carrier Transport Mechanism

Stable Electron‐Selective Contacts for Crystalline Silicon Solar Cells Enabling Efficiency over 21.6%

Al2O3/Ag/Al2O3 Passivating and Conducting Stacks for Crystalline Silicon Solar Cells

Low-temperature Ta-doped TiOx Electron-Selective Contacts for High-Performance Silicon Solar Cells