Abstract:During the formation of Si nanocrystals (Si NC) in Si$_x$C$_{1-x}$ layers via solid-phase crystallization, the unintended formation of nanocrystalline SiC reduces the minority carrier lifetime and therefore the performance of Si$_x$C$_{1-x}$ as an absorber layer in solar cells. A significant reduction in the annealing time may suppress the crystallization of the SiC matrix while maintaining the formation of Si NC. In this study, we investigated the crystallization of stoichiometric SiC and Si-rich SiC using conventional rapid thermal annealing (RTA) and nonequilibrium millisecond range flash lamp annealing (FLA). The investigated Si$_x$C$_{1-x}$ films were prepared by plasma-enhanced chemical vapor deposition and annealed at temperatures from 700${\deg}$C to 1100${\deg}$C for RTA and at flash energies between 34 J/cm$^2$ and 62 J/cm$^2$ for FLA. GIXRD and FTIR were conducted to investigate hydrogen effusion, Si and SiC NC growth, and SiC crystallinity. Both the Si content and the choice of the annealing process affect the crystallization behavior. It is shown that under certain conditions, FLA can be successfully utilized for the formation of Si NC in a SiC matrix, which closely resembles Si NC in a SiC matrix achieved by RTA. The samples must have excess Si, and the flash energy should not exceed 40 J/cm$^2$ and 47 J/cm$^2$ for Si$_{0.63}$C$_{0.37}$ and Si$_{0.77}$C$_{0.23}$ samples, respectively. Under these conditions, FLA succeeds in producing Si NC of a given size in less crystalline SiC than RTA does. This result is discussed in terms of nucleation and crystal growth using classical crystallization theory. For FLA and RTA samples, an opposite relationship between NC size and Si content was observed and attributed either to the dependence of H effusion on Si content or to the optical absorption properties of the materials, which also depend on the Si content.

Rapid thermal annealing and crystallization mechanisms study of silicon nanocrystal in silicon carbide matrix

Diamond Nanocrystals and Amorphous SiOx Nanowires Formed by Rapid Thermal Annealing of Carbon Film

Formation of silicon nanocrystals in silicon carbide using flash lamp annealing

Post-Growth Rapid Thermal Annealing Effect on Hydrogenated Amorphous Silicon Carbide Thin Film

Crystallization and Raman Shift of Array-Orderly Silicon Nanowires after Annealing at High Temperature

ENHANCED FORMATION OF Si NANOCRYSTALS IN SiO2 BY LIGHT-FILTERING RAPID THERMAL ANNEALING

Crystallization of amorphous silicon thin films: The effect of rapid thermal processing pretreatment

The Effect Of Thermal Annealing On Crystallization In A-Si : H/Sio2 Multilayers By Using Layer By Layer Plasma Oxidation

Influence of annealing on microstructures and photoluminescence of nano-composite silicon film

Effect of annealing on microstructure and photoluminescence of nano-composite silicon film

Crystallization and Disappearance of Defects of the Annealed Silicon Nanowires

Omparisons of Silicide Formation by Rapid Thermal Annealing and Conventional Furnace Annealing

Characterization of the Interface Region During the Agglomeration of Silicon Nanocrystals in Silicon Dioxide

Microstructure and Conductivity of Large Area Nanocrystalline Silicon Films Grown by Specially Designed Thermal-Assisted Chemical Vapor Deposition

Crystallized Silicon Nanostructures - Experimental Characterization and Atomistic Simulations

Evolution of Si Suboxides into Si Nanocrystals During Rapid Thermal Annealing As Revealed by Xps and Raman Studies

Crystallization of As-Deposited Amorphous Silicon Films on Glass Prepared by Magnetron Sputtering with Different Substrate Biases and Temperatures

Rapid thermal annealing of Si paste film and pn-junction formation

Effect of High-Temperature Annealing on Raman Characteristics of Silicon Nanowire Arrays

Annealing Effect on Optical and Electronic Properties of Silicon Rich Amorphous Silicon-Carbide Films

Crystallization of Ion-Beam-synthesized SiC Layer by Thermal Annealing