In‐situ elemental reaction‐regulated Ag2S films enable the best thermoelectric performances
Chengcheng Xing,Ruijuan Qi,Yi Chang,Xiaoming Ma,Yan Lei,Shuangquan Zang,Zhi Zheng
DOI: https://doi.org/10.1002/agt2.561
2024-04-24
Aggregate
Abstract:Based on the sulfurization route treated with direct metal surface elemental reaction solution, the continuous dense Ag2S films of different thicknesses were prepared on glass substrates, showing the best thermoelectric properties of such materials so far, the zT reaches 0.83 ± 0.30 near 600 K. Silver sulfide thin film, with excellent thermoelectric properties, is few reported due to the complex and time‐consuming high‐temperature or high‐pressure synthesis process. Here, a fast ionic conductor n‐type Ag2S film with good crystallinity and uniform density is prepared by sputtering metal Ag films of different thicknesses on glass and then reacting in S precursor solution at low temperature. At 450 K, β‐Ag2S films can be obtained and underwent a phase transition from α‐Ag2S monoclinic, which had a significant effect on their electrical and thermal properties. The grain size of Ag2S films increases with the increase of film thickness. Before and after the phase transition, the carrier concentration and mobility cause obvious changes in the electrical properties of Ag2S. The carrier concentration of body‐centered cubic phase β‐Ag2S is about three orders of magnitude higher than that of monoclinic phase α‐Ag2S, and the mobility is also 2–3 times that of the latter. Especially, after the phase transition, the conductivity of β‐Ag2S rises exponentially from the zero conductivity of α‐Ag2S and increases with the increase of temperature. The Ag2S film shows the highest figure of merit of 0.83 ± 0.30 at 600 K from the sample with ∼1600 nm thickness, which is the highest record among Ag2S‐based thermoelectric materials reported so far.
chemistry, multidisciplinary, physical,materials science