Fracture Behavior and Toughness of Fiber Reinforced Thermoset Composites
Alak Kumar Patra,Indrajit Ray
DOI: https://doi.org/10.1007/978-981-16-0642-7_6
2021-01-01
Abstract:The fiber reinforced polymer composites (FRPC) are being widely used in several advanced engineering structures ranging from civil infrastructure to aircraft, spacecraft, ships, cars and in many other outdoor and household applications. The major advantage is its high specific strength, stiffness, and durability leading to sustainable applications. Thermoset resins have advantages of retaining shape and strength at a higher temperature and harsh environment and lower life-cycle cost compared to thermoplastic resins. However, the knowledge of their behaviors during fracture failures are essential to properly evaluate the performance of thermoset composites. This chapter is divided into following five sections: Sect. 1 provides the introduction; Sect. 2 discusses the fracture mechanism of FRP’s from micromechanics and global response of components or structure as a whole. The detailed information on general fracture mechanics approach including different modes of fracture, fracture failure procedures, fracture mechanics approach in FRC problems, fracture under compression, and failures at different scales will be provided. Section 3 elaborates on various failure theories such as micromechanical failure of FRP with UD lamina, anisotropic failure theory including theory of maximum stress, maximum strains, deviatoric strain energy theory, theory of tensor polynomial, failure for damage mechanism, failures under creep, fatigue and rupture, high strain rate failures. Section 4 covers the various modes of experimental investigations on FRPC including mode I, mode II, mode III, and mixed mode fracture toughness.