Abstract:Pure copper is very soft, however, hardening the pure copper with most strengthening mechanisms leads to a significant reduction in electrical conductivity. Grain refinement is a better strengthening mechanism to maintain high enough electrical conductivity. Plastic deformation at room temperature followed by post-annealing is one of the best methods to achieve fine-grained metals and alloys. In this research, the high-temperature annealing behavior of cold-rolled electrolytic tough-pitch (ETP) copper sheets was studied. 90 % asymmetric cold rolling followed by high-temperature post-annealing at 673 K for 1, 2, 5, 10, 30, 60, and 120 min were applied on the copper. The microstructure was significantly changed with increasing annealing time from 1 to 2 min owing to full recrystallization. With increasing the annealing duration, the grain size is increased. The formation of equiaxed grains with a smaller size (∼9 μm) compared to the full-annealed (initial) sample (∼68 μm) is observed after the longest time of post-annealing (120 min) due to the pinning effect of Cu2O particles. The post-annealed copper sheets processed by asymmetric rolling (in this work) exhibited a more homogeneous microstructure through the thickness compared to the symmetric rolling due to more uniform stored strain energy. The results showed that the first deformed grains that undergo recrystallization during post-annealing are Goss-oriented grains. With an increase in the post-annealing time, the S and Copper components were eliminated and a strong Cube and P texture orientations were formed. Interestingly, after 1 min of post-annealing, the yield and tensile strength enhanced to 410.2 MPa and 418.6 MPa owing to the annealing hardening phenomenon. The hardness and strength reached a constant value after the post-annealing for 10 min and above. With increasing the post-annealing duration, the central area of fracture surfaces (consisting of ductile dimples) became larger and the outer region (consisting of flat surfaces and shear dimples) became smaller, showing a shift towards perfect ductile fracture. With the increase of post-annealing time from 1 min to 120 min, the electrical conductivity was increased from 77.6 to 97.5 %IACS. The presence of the Cube texture increased the electron mobility compared to the P orientation, by reducing the mean distance that they can travel without scatter. From the obtained results, it can be concluded that the asymmetric cold rolling followed by high-temperature post-annealing is capable of strength improvement and maintaining electrical conductivity in copper.

Improvement in Strength and Ductility of Asymmetric-Cryorolled Copper Sheets Under Low-Temperature Annealing

Effect of cryogenic impact deformation and subsequent annealing on microstructure and microhardness of pure copper

Reforming Nanostructured CuAg Alloy to Improve Ductility and Electrical Conductivity

Mechanical Properties of Rolled Copper Foils in Cryogenic and Room‐Temperature Environments

Low‐Temperature Annealing of Asymmetrically Cold‐Rolled Electrolytic Tough‐Pitch Copper: Anneal Hardening and Bimodal Microstructure

High-temperature annealing behavior of cold-rolled electrolytic tough-pitch copper

Achieving High Strength and Tensile Ductility in Pure Nickel by Cryorolling with Subsequent Low-Temperature Short-Time Annealing

Tensile Properties of Cryorolled Cu/Al Clad Sheet with an SUS304 Interlayer after Annealing at Various Temperatures

Mechanical property enhancement and microstructure evolution of an Al-Cu-Li alloy via rolling at different temperatures

Effects of Cold Rolling Path on Recrystallization Behavior and Mechanical Properties of Pure Copper During Annealing

Mechanical Properties and Microstructure of Rolled and Electrodeposited Thin Copper Foil

Effect of low temperature annealing on microstructure and properties of copper foil

Effect of Annealing on the Microstructure, Texture and Tensile Deformation Properties of Cu–3 Wt%ag–0.5 Wt%zr Thin Sheets Rolled at Room and Cryogenic Temperature

The mechanical properties of OFHC copper and CuCrZr alloys after asymmetric rolling at ambient and cryogenic temperatures

Effect of cryo-rolling on mechanical properties and microstructure of pure copper

High Strength and High Electrical Conductivity CuMg Alloy Prepared by Cryorolling

High strength high conductivity copper prepared by C-ECAP and Cryo-rolling

Effect of cryogenic rolling and multistage thermo-mechanical treatment on the microstructure and properties of the Cu-0.4Cr-0.39Zn-0.1Mg-0.07Zr alloy

Cryogenic Formability of a Solution-Treated Aluminum Alloy Sheet at Low Temperatures

Microstructure and Texture Evolution in Cold-Rolled and Annealed Oxygen-Free Copper Sheets

Effect of cryogenic temperature on the deformation mechanism of a thin sheet of pure copper at the mesoscale