Abstract:Heterogeneous metallic structures constitute a novel class of materials with excellent mechanical properties. However, the existing process for obtaining heterostructures from a single material does not meet large-scale industrial requirements. In this study, a pure copper heterostructured laminate (HSL) composed of a surface elongated-grain layer and a central equiaxed-grain layer was fabricated by rolling bonding and annealing. To study the effect of the interface on the mechanical properties of gradient-structured materials, both laminate metal composite (LMC) and non-composite laminate (NCL) were fabricated by cold-rolling pretreatment of the center layer (60% reduction) and cold-rolling bonding of the whole blank (67% reduction). Then, the HSL was obtained by controlling the post-annealing regimes, the microstructure of each layer was optimized, and a larger degree of microstructural heterogeneities, such as grain size, misorientation angle, and grain orientation, was obtained, which resulted in obvious mechanical differences. Tensile tests of the HSL, surface layer, center layer, and NCL specimens revealed that the HSL annealed at 300 °C for 1 h had a significantly higher strength than the center layer and a higher elongation than the surface layer. The HSL had a tensile strength and elongation at fracture of 278.08 MPa and 46.2%, respectively, indicating a good balance of strength and plasticity. The improved properties were primarily attributed to the strengthening or strain hardening due to the inhomogeneous deformation of the heterogeneous layers in the laminate and the mutual constraint acquired by the distinct layers with strong mechanical differences. The HSL had an interfacial bonding strength of 178.5 MPa, which played a vital role in the coordinated deformation of the heterogeneous layers. This study proposes an HSL design method that effectively simplifies the process of obtaining heterostructures in homogeneous materials by controlling the cumulative deformation of the surface and center layers.

High Strength and High Ductility Copper Obtained by Topologically Controlled Planar Heterogeneous Structures

Investigation of Mechanical Properties and Microstructural Evolution in Pure Copper with Dual Heterostructures Produced by Surface Mechanical Attrition Treatment

Simulating Size and Volume Fraction-Dependent Strength and Ductility of Nanotwinned Composite Copper

Microstructures and mechanical properties of Cu–Ti alloys with ultrahigh strength and high ductility by thermo-mechanical treatment

A dual heterogeneous laminated microstructure design for improving the mechanical properties and electrical conductivity of copper alloys

Strengthening mechanisms in heterostructured copper films with highly (220)-oriented vertical nanotwins

Towards enhanced strength-ductility in pure copper by fabricating hetero grain composite laminates

Achieving high strength and high conductivity synergy through hierarchical precipitation stimulated structural heterogeneities in a Cu-Ag-Zr alloy

A promising structure for fabricating high strength and high electrical conductivity copper alloys

Excellent Mechanical Properties and High Electrical Conductivity of Cu-Co-Si-Ti Alloy Due to Multiple Strengthening

Tuning heterogeneous geometric microstructure of Cu-based materials via powder metallurgy for improving high synergistic strengthening and electrical conductivity

Fabrication of high-strength metallic materials with heterostructure prepared via flow control extrusion

Additively Manufactured Copper Alloy with Heterogeneous Nanoprecipitates-Dislocation Architecture for Superior Strength-Ductility-Conductivity Synergy

High strength high conductivity copper prepared by C-ECAP and Cryo-rolling

Effect of G-phase and heterogeneous deformation-induced strengthening on the mechanical properties of Cu-20Ni-20Mn-2Fe-1Si alloy

Enhancing the interface strength of additively manufactured 316 L/CuSn10 bimetallic components through heterogeneous microstructures

Mechanical Properties Optimization and Microstructure Analysis of Pure Copper Heterostructured Laminates via Rolling

Achieving strength-ductility synergy in Al-4.5 wt%Cu binary alloy through semisolid isothermal treatment coupled with ECAP

Simultaneous enhancement of strength and ductility by combining heterogeneous microstructure and nanoprecipitates

Selective Laser Melting of High Relative Density and High Strength Parts Made of Minor Surface Oxidation Treated Pure Copper Powder

Enhancement of ultimate tensile strength and ductility of copper matrix composites using a low content of single-wall carbon nanotubes