Structural and magnetic properties of the nanocrystalline alloy Fe86Zr7Cu1B6

D. R. dos Santos,I. L. Torriani,F. C. S. Silva,M. Knobel

DOI: https://doi.org/10.1063/1.371784

IF: 2.877

1999-12-15

Journal of Applied Physics

Abstract:A detailed study on the nanocrystallization and its correlation with the attractive soft magnetic properties of the alloy Fe86Zr7Cu1B6 (at %) is presented. Melt-spun amorphous ribbons were submitted to Joule heating for a short time interval (ta=50 s) with different direct current values. The electrical resistance measured during heating showed strong variations associated with the nucleation and growth of α-Fe nanocrystals. From x-ray diffraction line profile analysis we obtained the average grain size, crystalline volume fraction, grain size distribution function, and lattice distortions for different annealing currents. The results display an excellent agreement with the magnetic characterization (ac initial permeability and dc hysteresis loops), showing that the optimum soft magnetic behavior is associated with the formation of about 50% in volume of the α-Fe nanophase. The extended x-ray absorption fine structure (EXAFS) technique was applied to study the evolution of the short-range ordering around Fe atoms. EXAFS spectra also showed the evolution from a disordered Fe environment to the bcc crystalline arrangement. The onset of crystallization determined from both techniques is slightly different, indicating that the nanocrystallization begins at the surface of the studied samples.

physics, applied

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the research on the structure and magnetic properties of the nanocrystalline alloy Fe_86Zr_7Cu_1B_6. Specifically, the author prepared amorphous Fe_86Zr_7Cu_1B_6 ribbons by the melt - quenching method and studied the nanocrystallization process of these materials after DC Joule - heating treatment and its relationship with excellent soft magnetic properties. The focus of the research is to perform short - time (50 seconds) Joule - heating on samples with different current values, observe and analyze the change in resistance during the heating process and the formation of the nanocrystalline phase, in order to understand the influence of the nanocrystallization process on the magnetic properties of the materials.

The main objectives of the paper include:
1. **Detailed study of the nanocrystallization process**: Through Joule - heating treatment, study the nanocrystallization process of amorphous Fe_86Zr_7Cu_1B_6 ribbons, especially the formation of the α - Fe nanocrystalline phase.
2. **Relationship between magnetic properties and nanocrystallization**: Explore how factors such as the volume fraction of the nanocrystalline phase and the grain size distribution formed during the nanocrystallization process affect the soft magnetic properties of the materials.
3. **Characterization of structure and magnetic properties**: Use techniques such as X - ray diffraction (XRD) and extended X - ray absorption fine structure (EXAFS) to perform detailed characterization and analysis of the structure and magnetic properties of the samples.

Through these studies, the author hopes to reveal the key parameters in the nanocrystallization process, such as the optimal volume fraction of the nanocrystalline phase and the grain size, in order to optimize the soft magnetic properties of the materials, thereby providing theoretical and technical support for the practical application of nanocrystalline materials.