Nanocrystalline Fe(Co)ZrMoBCu soft magnetic alloys: A transmission electron microscopy study of the microstructures

Yaming Sun,Jiaxin Li,Zhiqun Wang,Lihua Liu

DOI: https://doi.org/10.1016/j.jallcom.2024.174350

IF: 6.2

2024-04-05

Journal of Alloys and Compounds

Abstract:Nanocrystalline Fe 81 Zr 7 Mo 2 B 9 Cu 1 and Fe 40.5 Co 40.5 Zr 7 Mo 2 B 9 Cu 1 alloy ribbons were prepared by annealing the as-quenched amorphous alloys at their first exothermic peak temperature. The primary crystallization phases of Fe 81 Zr 7 Mo 2 B 9 Cu 1 and Fe 40.5 Co 40.5 Zr 7 Mo 2 B 9 Cu 1 consisted of nanoscale body-centered cubic α-Fe and α -FeCo grains, respectively The microstructures and compositions were analyzed via transmission electron microscopy (TEM) and scanning transmission electron microscopy (STEM), and area maps were obtained through energy-dispersive spectroscopy (EDS). The addition of Co decreased the mean grain size ( D ) and broadened the grain-size distribution (σ). The effect of the addition of Co on the Cu clusters and element distribution was studied in detail. Scanning transmission electron spectroscopy combined with energy-dispersive spectroscopy revealed that both alloys contained Cu clusters; the Fe 40.5 Co 40.5 Zr 7 Mo 2 B 9 Cu 1 alloy exhibited a Cu-cluster density similar to that of the Fe 81 Zr 7 Mo 2 B 9 Cu 1 alloy. Both alloys contained relatively less Fe in their residual amorphous phases than in their nanocrystals, with the nanocrystals in Fe 40.5 Co 40.5 Zr 7 Mo 2 B 9 Cu 1 containing less Co than in the residual amorphous phase. Fe 40.5 Co 40.5 Zr 7 Mo 2 B 9 Cu 1 exhibited higher specific saturation magnetization ( M s ), specific remanent magnetization ( M r ) and larger coercivity ( H c ) than Fe 81 Zr 7 Mo 2 B 9 Cu 1 .

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering