Abstract:The characteristics of the interface are the key factors that determine the mechanical properties and fracture behavior of fiber-reinforced ceramic matrix composites. Design and preparation of coatings which can preserve fiber strength and maintain appropriate interfacial bonding strength are of great challenges. LaPO4 coating is a promising weak interface coating for oxide fiber reinforced oxide ceramic matrix composites. Through this coating, the toughening mechanism of the composite such as fiber pulling out and fiber debonding is triggered. The LaPO4 coating was deposited on the surface of alumina-based fibers by a solution precursor heterogeneous precipitation method. The effects of different precursors and different deposition temperatures on fiber strength were studied, and the mechanism of the strength degradation of the coated fiber was analyzed. It was found that the fibers coated with phytic acid precursor and deposited at 90 °C had the highest tensile strength compared to other coated fibers. The retention of strength is attributed to its loosely stacked coating. Besides, a single fiber pullout test was carried out to evaluate the effect of the coating on the interface of the composites. The results show that the composites coated by depositing citric acid precursor and phytic acid precursor at 90 °C can reduce the interfacial bonding strength by 32.5% and 46.7%, respectively compared to uncoated composites. This study has potential application value in the preparation of ceramic matrix composites used in oxidation and high temperature environments.

Continuous alumina fiber-reinforced yttria-stabilized zirconia composites with high density and toughness

Activating Continuous Dislocation Pinning Enhanced Toughness of Nanocomposite Coating Through Specially Oriented Semicoherent Heterointerface Lattice Distortion

The Influence of Platelet‐Like LaMgAl11O19 on the Toughness of 3 Mol% Yttria Partially Stabilized Zirconia Ceramic

LaPO4 coating on alumina-based fiber: Strength retention of fiber and improvement of interfacial performances

Al 2 O 3 -fiber-reinforced porous YSZ ceramics with high mechanical strength

Influence of La2O3 Addition on Microstructure and Mechanical Properties of Alumina-Dispersed Zirconia

Enhanced Toughness Of Zirconia Ceramics With Graphene Platelets Consolidated By Spark Plasma Sintering

Facile method for preparing lamellar structured alumina-zirconia ceramics with high toughness

A novel method for fabricating brick-mortar structured alumina-zirconia ceramics with high toughness

Fabrication and Properties of Porous Yttria-Stabilized Zirconia Ceramics

Hot-pressed ZrB2–SiC–YSZ Composites with Various Yttria Content: Microstructure and Mechanical Properties

Effect of Y2O3-stabilized ZrO2 Whiskers on the Microstructure, Mechanical and Wear Resistance Properties of Al2O3 Based Ceramic Composites

Fracture Toughness of Al2O3‐Particle‐Dispersed Y2O3‐Partially Stabilized Zirconia

Fabrication of highly translucent yttria-stabilized zirconia ceramics using stereolithography-based additive manufacturing

Microstructure and thermal shock resistance of LaPO4-ZrO 2

A Novel Way to Fabricate Highly Porous Fibrous YSZ Ceramics with Improved Thermal and Mechanical Properties

Highly Reliable Yttria‐stabilized Zirconia Prepared by Direct Coagulation Casting‐high Valence Counter Ions Using Calcium Polyphosphate

Properties of a Pressureless Sintered 2Y-TZP Material Combining High Strength and Toughness

Preparation and mechanical properties of NiCr-Al 2O 3-ZrO 2(8Y) ceramic composites

Enhanced Mechanical Properties Of Machinable Lapo4/Al2o3 Composites By Spark Plasma Sintering

Porous LSCF/Dense 3YSZ Interface Fracture Toughness Measured by Single Cantilever Beam Wedge Test