The Influence of the Silicon Content on the Formation of Fe23B6 Metastable Phases in Fe65Co11−xB20SixZr2Hf2 Bulk Amorphous Alloys

Marcin Nabiałek,Bartłomiej Jeż,Katarzyna Błoch
DOI: https://doi.org/10.1007/s11661-020-05894-y
2020-07-07
Metallurgical and Materials Transactions A
Abstract:This study aims to determine the effect of addition of a small quantity of Si on the formation of nanocrystalline structure in rapidly cooled Fe-Co-B alloys. As part of the work, the following alloys were produced using a method involving the forcing of each respective liquid alloy into a copper mold: Fe<sub>65</sub>Co<sub>11−<i>x</i></sub>B<sub>20</sub>Si<sub><i>x</i></sub>Zr<sub>2</sub>Hf<sub>2</sub> (where: <i>x</i> = 0; 0.25; 0.5; 0.75; 1). Analysis of recorded X-ray diffraction patterns confirmed that a nanocrystalline structure was obtained in the alloys. The intensity of the diffraction reflections was found to change with changing Si content. The Fe<sub>23</sub>B<sub>6</sub> crystalline phase was present in the volume of each alloy. This phase has soft magnetic properties. The presence of the Fe<sub>23</sub>B<sub>6</sub> phase was confirmed by measurements of the magnetic polarization of saturation as a function of temperature.
What problem does this paper attempt to address?