Fabrication and Soft Magnetic Properties of Fe–B–Si–Zr/Hf–Cu Nanocrystalline Alloys with High Glass-Forming Ability

Yaoxiang Geng,Yingmin Wang,Yuxin Wang,Zhijie Zhang,Hongbo Ju,Lihua Yu,Junhua Xu

DOI: https://doi.org/10.1007/s12540-020-00647-3

IF: 3.451

2020-03-03

Metals and Materials International

Abstract:The effects of minor alloying addition of Cu on the glass-forming ability and crystallization process of Fe71.7−xB16.7Si8.3Zr3.3Cux and Fe72.5−xB16.7Si8.3Hf2.5Cux (x = 0, 0.3, 0.7, 1.0 and 1.3; at%) alloys were investigated. It was found that the critical glass formation size of rod samples gradually decreased from 2.5 to 1 mm with increasing Cu content in these alloys. Single α-Fe phase nanocrystalline alloys were obtained after isothermal annealing the Fe–B–Si–Zr/Hf–Cu glassy alloys containing 0.7–1.0 at% Cu. The Fe71B16.7Si8.3Zr3.3Cu0.7 alloy exhibited good soft magnetic properties with a high saturation magnetization (~ 1.22 T) and a low coercive force (~ 0.6 A/m) after annealing at 853 K for 10 min due to the precipitation of α-Fe nanoparticles of 8 nm size in the glassy matrix. The structural evolution on annealing and the variation tendencies against Cu content of the glass transition temperature, thermal stability and glass-forming ability of the Fe–B–Si–Zr/Hf–Cu amorphous alloys were discussed using a dual-cluster local structure model.Graphic

materials science, multidisciplinary,metallurgy & metallurgical engineering