Abstract:In this paper, the rolling contact fatigue (RCF) failure mechanism of ZC-L cast steel wheels was analyzed by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). The results show that obvious fatigue flaking is formed on the macroscopic surface of the wheel tread after RCF failure. The RCF cracks are formed at the maximum shear stress region of the sun-surface of the wheel (1∼5 mm below the tread). There are a lot of subsurface white etching microstructure (WEM) and obvious casting defects in the subsurface of the wheel tread. The RCF cracks are mainly formed at the interface between the subsurface WEM and the matrix and at the edge of the casting defects. The subsurface WEM is composed of nano-ferrite grains and residual cementite, and its hardness is about 920HV, which is much higher than that of the matrix structure. During the wear process, the plastic deformation of the subsurface WEM and the matrix is not coordinated, resulting in the formation of RCF cracks. As a hard phase, the hardness of casting defects is much higher than that of matrix. In the process of wear, under the action of subsurface stress, the casting defects can cause obvious plastic deformation in the soft orientation region at the edge of the casting defects. When the plastic deformation reaches the plastic limit, the RCF cracks are formed at the edge of the inclusions due to ratchet failure. The stress at the crack tip is caused by the RCF crack propagation at the edge of inclusions will further lead to the refinement of the microstructure at the edge of the RCF crack. Under the action of the subsurface contact stress, the subsurface WEM and casting defects are the main reasons leading to the RCF failure of the ZC-L casting wheel. Improving the microstructure uniformity and reducing casting defects are the main methods to improve the fatigue property of casting wheels.

Dark etching regions under rolling contact fatigue: a review

Evaluation of Dark Etching Regions for Standard Bearing Steel under Accelerated Rolling Contact Fatigue

Further Investigations and Parametric Analysis of Microstructural Alterations under Rolling Contact Fatigue

Development of White Etching Bands under Accelerated Rolling Contact Fatigue

A Multiscale Overview of Modelling Rolling Cyclic Fatigue in Bearing Elements

The Evolution of White Etching Cracks (WECs) in Rolling Contact Fatigue-Tested 100Cr6 Steel

The origin of microstructural alterations in M50 bearing steel undergoing rolling contact fatigue

A new explanation of Rolling Contact Fatigue in bearing steels based on multiscale models

Hydrogen-accelerated white etching area formation in bearings under rolling contact fatigue

Micromechanical response of dual-hardening martensitic bearing steel before and after rolling contact fatigue

A 3D Finite Element Model of Rolling Contact Fatigue for Evolved Material Response and Residual Stress Estimation

Micromechanism of cumulative damage in bearing steels under Rolling Contact Fatigue

Finite Element Analysis Simulation of the Effect of Induction Hardening on Rolling Contact Fatigue

Influence of original microstructure on rolling contact fatigue property of D2 wheel steel

The effect of retained austenite on rolling/sliding contact fatigue of high carbon steel

A study on the of rolling contact fatigue mechanism of ZC-L cast wheel steel

Microstructural-based analysis of the unexpected differences in rolling contact fatigue behavior between SAE52100 and SAE4320

An electron backscatter diffraction investigation on microstructural evolution of pearlite wheel steel near rolling contact fatigue crack tip

Re‐recognition of Deep Spalling Damage Mechanism of Rolling Contact Fatigue under Heavy Load

Rolling contact fatigue failure mechanism of bearing steel on different surface roughness levels under heavy load

A study of local microstructure decay in GCr15 due to rolling contact