Abstract:Subsurface microstructural alterations are formed in the later stages of rolling contact fatigue (RCF) under high contact pressure. The subsurface changes observed as a dark contrast under optical microscopy are classified as Dark Etching Regions (DERs). Despite the fact that DERs have been presented for several decades, the understanding of its development and growth is yet to comprehend. Current research employed a modified high-speed microprocessor rotary tribometer to conduct systematic RCF study under accelerated testing conditions with variable temperatures and contact pressures. Comprehensive RCF data has been acquired, analysed and is reported for the very first time with ball-on-ball point contact loading conditions. The subsurface microscopic investigations have shown the ongoing progression and development of DER extent and are reported to be associated with the accumulation of plasticity during RCF. The comparison of the DER with the responsible stress components have revealed that DER formation is more closely related to the von Mises stresses when superposed with residual stresses. The experimentally observed area fraction of dark etching zones has been evaluated in terms of DER% and compared with the dislocation assisted carbon diffusion model for DER formation. The overprediction of the numerical model in comparison with the presented results in current research manifests its limitations which can be improved with the incorporation of cyclic plasticity governed by evolved von Mises stresses. Detailed evaluated DER results are presented as 3D DER% maps incorporating the combined effects of contact stress, temperature and rolling cycles simultaneously which enables an in-depth RCF understanding within microstructural context and therefore can be used as guidelines for DER formation models.

Hydrogen-accelerated white etching area formation in bearings under rolling contact fatigue

Peridynamic Modeling of Hydrogen-Assisted White Etching Cracks in Bearing Steel under Rolling Contact Fatigue

Dark etching regions under rolling contact fatigue: a review

Morphological effect of retained austenite microstructure on hydrogen diffusion under contact loading of bearings

The Evolution of White Etching Cracks (WECs) in Rolling Contact Fatigue-Tested 100Cr6 Steel

The origin of microstructural alterations in M50 bearing steel undergoing rolling contact fatigue

A Study on Decisive Early Stages in White Etching Crack Formation Induced by Lubrication

A new explanation of Rolling Contact Fatigue in bearing steels based on multiscale models

Further Investigations and Parametric Analysis of Microstructural Alterations under Rolling Contact Fatigue

Effects of retained austenite and hydrogen on the rolling contact fatigue behaviours of carbide-free bainitic steel

Evaluation of Dark Etching Regions for Standard Bearing Steel under Accelerated Rolling Contact Fatigue

Effect of Hydrogen on Very High Cycle Fatigue Behavior of a Low-Strength Cr-Ni-Mo-V Steel Containing Micro-Defects

White etching area damage induced by shear localization in rolling contact fatigue of bearing steel

Influence of Lubricated Rolling/Sliding Tribotesting on Hydrogen Trapping in 100Cr6 Bearing Steel

Development of White Etching Bands under Accelerated Rolling Contact Fatigue

Prediction of Work Hardening in Bearing Steels Undergoing Rolling Contact Loading with a Dislocation-Based Model

Micromechanism of cumulative damage in bearing steels under Rolling Contact Fatigue

Rolling contact fatigue failure mechanism of bearing steel on different surface roughness levels under heavy load

Effect of spatial hardness distribution in rolling contact fatigue performance of bearing contacts

The effect of friction on surface crack initiation in rolling contact fatigue considering damage accumulation

Combined Effects of Structural Transformation and Hydrogen Passivation on the Frictional Behaviors of Hydrogenated Amorphous Carbon Films